Mechanical, tribological and anti-corrosive properties of polyaniline/graphene coated Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn alloys
Mechanical, tribological and anti-corrosive properties of polyaniline/graphene coated Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn alloys作者机构:Materials Science and Engineering Indian Institute of Technology Kanpur Kanpur 208016 India Centre for Material Science & Engineering National Institute of Technology Hamirpur Hamirpur 177005 India China-Canada Institute for Advanced Surface & Interface Science and Engineering Jiangsu University of Technology Changzhou 213001 China
出 版 物:《Journal of Materials Science & Technology》 (材料科学技术(英文版))
年 卷 期:2019年第35卷第8期
页 面:1767-1778页
核心收录:
学科分类:08[工学] 0817[工学-化学工程与技术] 0806[工学-冶金工程] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
基 金:funding from Space Technology Cell (IIT Kanpur and Indian Space Research Organisation)
主 题:Mg-Li alloys Scratch hardness Plowing hardness Wear resistance Corrosion protection efficiency Charge transfer resistance
摘 要:The mechanical,tribological and corrosion protection offered to Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn alloys by the epoxy coating containing polyaniline/graphene(PANI/Gr)pigments is undertaken in the current work.PANI/Gr containing coatings were observed to be strongly adherent with a higher scratch hardness(Hs)and plowing hardness(Hp),i.e.Hsof 0.43 GPa,and Hpof 0.61 GPa,respectively when compared to that of neat epoxy coating(Hsof 0.17 GPa,and Hpof 0.40 GPa,respectively).Due to their higher Hsand Hpvalues,PANI/Gr based coatings displayed an enhanced wear resistance(Wear volume,Wv=4.53×10^-3 m^3)than that of neat epoxy coating(Wv=5.15×10^-3 m^3).The corrosion protection efficiency in corrosive environment of 3.5 wt%NaCl solution was obtained to be99% for PANI/Gr containing coatings when compared to that of neat epoxy coating.The charge-transfer resistance(R(ct))of the PANI/Gr containing coatings were estimated to be10^6 cm^2,which indicates their highly protective nature when compared to that of neat epoxy coating(R(ct)10^5 Ω cm^2).Hence,PANI/Gr containing coatings can be potentially used for wear resistance and corrosion protection applications in marine environments.