Effect of 2–6 at.% Mo addition on microstructural evolution of Ti-44Al alloy

作     者：S.Z.Zhang Z.W.Song J.C.Han C.J.Zhang P.Lin D.D.Zhu F.T.Kong Y.Y.Chen 

作者机构：School of Materials Science and Engineering Taiyuan University of Technology Shanxi Key Laboratory of Advanced Magnesium-Based Materials Taiyuan University of Technology School of Mechanical Engineering Taiyuan University of Technology School of Mechanical Engineering Quzhou University State Key Laboratory for Advanced Welding and Jointing Harbin Institute of Technology 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：2018年第34卷第7期

页      面：1196-1204页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：supported financially by the National Natural Science Foundation of China (Nos. 51604191, 51504163 and5 1501100) the Natural Science Foundation for Young Scientists of Shanxi Province, China (No. 201701D221075) the State Key Laboratory for Advanced Metal and Materials foundation (No. 2014-ZD06) the Special/Youth Foundation of Taiyuan University of Technology (Nos. 2015QN014, 2013T004 and 2013T003) the financial support of the Qualified Personnel Foundation of Taiyuan University of Technology (Nos. tyutrc201342a and tyutrc201343a) 

主　　题：Phase transformation Titanium aluminides Heat treatment Microstructure evolution,β/βo phase 

摘      要：In order to understand the effect of Mo alloying on the microstructural evolution of TiAl alloy, the as-cast microstructure, heat treated microstructure characteristic, and hot compression microstructure evolution of Ti-44Al alloy have been studied in this work. The as-cast microstructure morphology changes from （γ＋α2） lamellar colony and β/β0＋γ mixture structure to β/β0 phase matrix widmannstatten structure, when Mo content increases from 2 at.% to 6 at.%. Affected by the relationship between β phase and α90℃phase, the angles between the lamellar orientation and the block β/β0 phase are roughly at 0℃, 45℃ and 90℃. Comparing with heat treatment microstructure, the hot compression microstructure contains less β/β0 phase, however, theβ/β0 phase containing 2Mo alloy and 3Mo alloy hot compressed at 1275 ℃ has the inverse tendency. In addition, （α2 ＋γ） colony is decomposed by the discontinuous transformation.2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science ＆ Technology.