Analysis of the Adsorption of Toxic Chromium (VI) by Untreated and Chitosan Treated Banana and Areca Fiber
Analysis of the Adsorption of Toxic Chromium (VI) by Untreated and Chitosan Treated Banana and Areca Fiber作者机构：Department of Yarn Engineering Bangladesh University of Textiles Dhaka Bangladesh Department of Applied Science & Chemical Engineering University of Dhaka Dhaka Bangladesh Department of Fabric Engineering Bangladesh University of Textiles Dhaka Bangladesh Institute of Radiation and Polymer Technology Bangladesh Atomic Energy Commission Dhaka Bangladesh
出 版 物：《Journal of Textile Science and Technology》 (纺织科学与技术（英文）)
年 卷 期：2020年第6卷第2期
页 面：81-106页
学科分类：081704[工学-应用化学] 07[理学] 070304[理学-物理化学(含∶化学物理)] 08[工学] 0817[工学-化学工程与技术] 0703[理学-化学]
主 题：Adsorption Heavy Metal Chitosan Banana Fiber Areca Fiber Toxicity
摘 要：This paper work involves bunch experiments to investigate the effect of contact time, pH, and adsorbent dose on the extent of adsorption by bio-composites. Adsorption capacity of Chromium (VI) onto chitosan coated with banana and areca fiber was investigated in a batch system by considering the effects of various parameters like contact time, initial concentration, pH and adsorbent dose. The chitosan and fibers (banana and areca) were then cross-linked with glutaraldehyde to remove chromium [Cr (VI)] from water via static adsorption. It was found that optimum chromium absorption capacity of chitosan was assessed at pH of 2.5 to 4.5 and contact time of 30 to 180 minutes for raw banana and areca fiber and for chitosan treated banana & areca fiber. Though optimum adsorption of chromium of chitosan was measured 34.17 ppm (85.42%) from a 100 ml solution containing 40 parts per million (ppm) of Cr (VI) at 120 minutes, pH of 3.0 and 120 milligram (mg) adsorbent dose size, use of composite will be more favorable in the point of environmental concern as well as low cost because chitosan preparation is comparatively costly then banana and areca fiber. On the other hand, untreated banana and areca fiber optimum adsorption of chromium measured 3.65 ppm (9.1%) at 180 min and, pH of 4.5 and 140 mg adsorbent dose size and 3.76 ppm (9.4%) at 180 min, pH of 4.5 and 160 mg adsorbent dose size respectively. In case of chitosan treated banana fiber, it was observed that adsorption was increased from 17.664 to 30.057 (75.14%). On the other hand, for areca fiber with chitosan, it was observed that adsorption was increased from 21.664 to 30.156 (75.39%) ppm. The Langmuir and Freundlich adsorption models were used for the mathematical description of the adsorption of chromium ion onto composites and it was found that the Langmuir adsorption isotherm was more fitted models which mean that a monolayer adsorption surface was created. After analyzing from IBM SPSS 25 software, we got the stand
维普期刊数据库