Solvent de binding of water soluble binder in powder injection moulding

作     者：Li Songlin(李松林) Huang Baiyun(黄伯云) Qu Xuanhui(曲选辉) Li Yimin(李益民) 

作者机构：Cent S Univ Technol State Key Lab Powder Met Changsha 410083 Peoples R China 

出 版 物：《中国有色金属学会会刊：英文版》 (Transactions of Nonferrous Metals Society of China)

年 卷 期：1999年第9卷第3期

页      面：578-581页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：国家863计划 

主　　题：powder injection moulding water soluble binders solvent debinding 

摘      要：The solvent debinding of water soluble binder in powder injection moulding (MIM) was investigated systematically, including the effects of solvent types, temperature and the thickness of green parts on the solvent debinding rate. After studying the debinding of a green part with a thickness of 4.26 mm, it was found that, the debinding rate of polyethylene glycol(PEG) in water and alcohol was high initially, and then decreased; however, it would increase with temperature increasing. At room temperature, the dissolution rate of PEG in water was higher than that in alcohol, but the latter would be much faster with temperature increasing because the debinding activation energy in alcohol was 51.44 kJ·mol -1 ·K -1 , much higher than 24.23 kJ·mol -1 ·K -1 in water. With a green part thickness larger than 4.26 mm, the debinding was controlled by diffusion; but with that smaller than 2.36 mm, the debinding was controlled by both dissolution and diffusion.