Synthesis and Properties of Ag-doped Titanium-10 wt% 45S5 Bioglass Nanostructured Scaffolds

作     者：K.Jurczyk A.Miklaszewski K.Niespodziana M.Kubicka M.U.Jurczyk M.Jurczyk 

作者机构：Department of Conservative Dentistry and PeriodontologyPoznan University of Medical Sciences Institute of Materials Science and EngineeringPoznan University of Technology Department of Genetics and Pharmaceutical MicrobiologyFaculty of PharmacyPoznan University of Medical Sciences Division Mother’s and Child’s HealthPoznan University of Medical Sciences 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：2015年第28卷第4期

页      面：467-476页

核心收录：

学科分类：08[工学] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：Biomaterials Nanocrystalline materials Titanium 45S5 Bioglass 

摘      要：A new kind of biomedical Ti-45S5 Bioglass-Ag nanocomposites and their scaffolds with antibacterial function was developed by the introduction of 1.5 wt% Ag into the Ti-10 wt% 45S5 Bioglass matrix. The microstructure, hardness and corrosion resistance in Ringer solution of the Ag-doped Ti-45S5 glass were investigated. The Vickers hardness of the bulk Ti-10 wt% 45S5 Bioglass-1.5 wt% Ag nanocomposites reached 480 HVo.3. Contact angles of water on the micro- crystalline Ti and nanostructured Ti-10 wt% 45S5 Bioglass-1.5 wt% Ag sample were determined and show visible decrease from 55.2° to 49.6°. In vitro tests culture of normal human osteoblast cells showed very good cells proliferation, colonization and multilayering. In vitro bacterial adhesion study indicated a significantly reduced number of bacteria （Staphylococcus aureus） on the bulk nanostructured Ti-10 wt% 45S5 Bioglass-1.5 wt% Ag plate surface in comparison with that on microcrystalline Ti plate surface. Development of porous Ti-10 wt% 45S5 Bioglass-1.5 wt% Ag scaffolds aims in enhancing bone ingrowth and prosthesis fixation.