Semisolid die forging process,microstructures and properties of AZ31 magnesium alloy mobile telephone shells

作     者：Ren-guo Guan Li-qing Chen Fu-rong Cao Zhan-yong Zhao Yong Ren 

作者机构：College of Materials and Metallurgy Northeastern University Shenyang 110004 China State Key Lab of Rolling and Automation Northeastern University Shenyang 110004 China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2011年第18卷第6期

页      面：665-670页

核心收录：

学科分类：080503[工学-材料加工工程] 0709[理学-地质学] 0819[工学-矿业工程] 08[工学] 0806[工学-冶金工程] 0708[理学-地球物理学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学（可授工学、理学学位）] 0702[理学-物理学] 080201[工学-机械制造及其自动化] 

基　　金：supported by the National Natural Science Foundation of China (Nos.51034002 and 50974038) the New Century Talents Support Program Project of the Ministry of Education of China (No.NCET-08-0097) 

主　　题：magnesium alloys semisolid forging microstructure mechanical properties fracture 

摘      要：A semisolid slurry of AZ31 magnesium alloy was prepared by vibrating wavelike sloping plate process,and the semisolid die forging process,microstructures,and properties of the magnesium alloy mobile telephone shell were *** semisolid forging process was performed on a YA32-315 four-column universal hydraulic *** microstructures were observed by optical microscopy,the hardness was analyzed with a model 450SVD Vickers hardometer,the mechanical properties was measured with a CMT5105 tensile test machine,and the fractograph of elongated specimens was observed by scanning electron microscopy （SEM）.The results reveal that with the increase of die forging force,the microstructures of the product become fine and dense.A lower preheating temperature and a longer dwell time are favorable to the formation of fine and dense *** optimum process conditions of preparing mobile telephone shells with excellent surface quality and microstructures are a die forging force of 2000 kN,a die preheating temperature of 250℃,and a dwell time of 240 *** solution treatment at 430℃ and aging at 220℃ for 8 h,the Vickers hardness is 61.7 and the ultimate tensile strength of the product is *** fractographs show the mixing mechanisms of quasi-cleavage fracture and ductile fracture.