Influence of Yb_2O_3-MgO on Mechanical Properties and Thermal Conductivity of Silicon Nitride Ceramics via Gas Pressure Sintering

作     者：LIN Sen YAO Dongxu XIA Yongfeng ZUO Kaihui YIN Jinwei ZENG Yuping 

作者机构：State Key Laboratory of High Performance Ceramics and Superfine MicrostructureShanghai Institute of CeramicsChinese Academy of Sciences Graduate School of Chinese Academy of Sciences 

出 版 物：《China's Refractories》 (中国耐火材料（英文版）)

年 卷 期：2015年第24卷第3期

页      面：34-39页

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：silicon nitride sintering mechanical properties thermal conductivity 

摘      要：In this work,Yb2O3 and Mg O were used as sintering aids in preparing silicon nitride ceramics by gas pressure sintering（ 0. 6 MPa N2atmosphere） to investigate how the amounts of Yb2O3- Mg O influence the mechanical properties and thermal conductivity of silicon nitride ceramics. The total contents of Yb2O3- Mg O added were 1 mol%,2 mol%,4 mol%,6 mol%,8 mol%,10 mol%,12 mol%,14 mol%,keeping the Yb2O3-Mg O molar ratio of 1 ∶ 1 steadily. Curves of the relative density,thermal conductivity and bending strength plotted against the aids content present a ‘mountain＇shape with a maximum at nearly 10 mol% aids. The fracture toughness increased with the amounts of additives up to10 mol% and decreased slightly thereafter. The mechanical properties and thermal conductivity were almost proportional to the amount of the additives before10 mol%. When the content of aids exceeded 10 mol%,it would weaken the mechanical properties and thermal conductivity of the ceramics. The optimum content of Yb2O3- Mg O was 10 mol% by gas pressure sintering（ 0. 6MPa） at 1 850 ℃ for 4 h,which led to a relative density of 98. 9%,a flexural strength of（ 966 ± 38）MPa as well as a fracture toughness of（ 6. 29 ± 0. 29）MPa·m1 /2and thermal conductivity of 82 W /（ m·K）.