Effect of Soaking Time on the Mechanical Properties of Annealed Cold-Drawn Low Carbon Steel
Effect of Soaking Time on the Mechanical Properties of Annealed Cold-Drawn Low Carbon Steel作者机构：Mechanical Engineering Department University of Ibadan Ibadan Nigeria
出 版 物：《Materials Sciences and Applications》 (材料科学与应用期刊（英文）)
年 卷 期：2012年第3卷第8期
页 面：513-518页
学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）]
主 题：Cold-Drawn Anneal Soaking-Time Tensile-Strength Yield-Strength Hardness Toughness Recrystallization Grain Growth
摘 要：The paper presents the results of investigation on the effect of soaking time on the yield strength, ductility and hardness properties of annealed cold-drawn low carbon steel. The low carbon steel cold-drawn at 40% deformation was annealed at 900 deg Celsius for soaking times of 10, 20, 30, 40, 50 and 60 minutes. Tensile, charpy and Brinnel hardness tests were conducted to determine the yield strengths, tensile strengths, impact strengths, ductility and hardness of the annealed steel with increasing soaking time. The yield strength, tensile strength, hardness and impact strength of the steel showed a continuous drop in value with increasing soaking time up to 60 minutes with a steep drop between 30 and 40 minutes. Ductility values followed the same decreasing trend up to 40 minutes soaking time after which the values started increasing again till 60 minutes soaking time. There was a linear relationship between the tensile strength and hardness of the material for different soaking times. This linear relationship was also observed for yield strength and hardness of the material.
维普期刊数据库