MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AZ91D EXTRUDED TUBE

作     者：B.Y. Yu C.L. Bao H.W. Song Z. Liu H.P. Yu 

作者机构：School of Materials Science and Engineering Shenyang University of Technology Shenyang 110023 China 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：2006年第19卷第3期

页      面：203-208页

核心收录：

学科分类：0817[工学-化学工程与技术] 0806[工学-冶金工程] 08[工学] 0807[工学-动力工程及工程热物理] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0802[工学-机械工程] 0703[理学-化学] 0811[工学-控制科学与工程] 

基　　金：2004221 009 

主　　题：magnesium tube microstructure tensile property 

摘      要：The effect of extrusion ratio on microstruetures and mechanical properties of magnesium alloy AZ91D extruded tube at 430℃ has been studied. After the evolution of microstracture and mechanical properties of AZ91D during extrusion were studied, the following parameters were obtained： tensile strength reached the climax value of 306.9MPa and elongation peak value of 10.1% at an extrusion ratio of 7.125, and with the increase of the extrusion ratio to 7.45, yield strength reached a top value of 285.795MPa with decreased tensile strength and elongation. It was concluded that mechanical properties of magnesium alloys AZ91D could be enhanced by adjusting the extrusion ratio near recrystallization.