Reaction mechanism for in-situ β-SiAlON formation in Fe3Si–Si3N4–Al2O3 composites

作     者：Hai-xia Qin Yong Li Li-xiong Bai Meng-long Long Wen-dong Xue Jun-hong Chen 

作者机构：School of Materials Science and Engineering University of Science and Technology Beijing Beijing 100083 China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2017年第24卷第3期

页      面：324-331页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：alumina ferrosilicon nitride SiAlON liquid sintering reaction mechanisins 

摘      要：In this work,Fe_3Si–Si_3N_4–Al_2O_3 composites were prepared at 1300°C in an N_2 atmosphere using fused corundum and tabular alumina particles,Al_2O_3 fine powder,and ferrosilicon nitride(Fe_3Si–Si_3N_4) as raw materials and thermosetting phenolic resin as a *** effect of ferrosilicon nitride with different concentrations(0wt%,5wt%,10wt%,15wt%,20wt%,and 25wt%) on the properties of Fe_3Si–Si_3N_4–Al_2O_3 composites was *** results show that the apparent porosity varies between 10.3% and 17.3%,the bulk density varies from 2.94 g/cm^3 and 3.30 g/cm^3,and the cold crushing strength ranges from 67 MPa to 93 *** the experimental conditions,ferrosilicon nitride,whose content decreases substantially,is unstable;part of the ferrosilicon nitride is converted into Fe_2C,whereas the remainder is retained,eventually forming the ferrosilicon *** assessment of the Si_5AlON_7 indicated that the ferrosilicon alloy accelerated the reactions between Si_3N_4 and α-Al_2O_3 fine powder and that Si in the ferrosilicon alloy was nitrided directly,forming β-Si Al ON *** addition,fused corundum did not react directly with Si_3N_4 because of its low reactivity.