Magnetic modification of diamagnetic agglomerate forming powder materials
Magnetic modification of diamagnetic agglomerate forming powder materials作者机构：Department of Nanobiotechnology Biology Centre ISB CAS Na Sadkach 7 370 05 Ceske Budejovice Czech Republic Regional Centre of Advanced Technologies and Materials Palacky University Slechtitelu 27 783 71 Olomouc Czech Republic Global Change Research Institute CAS Na Sadkach 7 370 05 Ceske Budejovice Czech Republic Department of Applied Chemistry Faculty of Agriculture University of South Bohemia Branisovska 1457 370 05 Ceske Budejovice Czech Republic
出 版 物：《Particuology》 (颗粒学报（英文版）)
年 卷 期：2016年第14卷第6期
页 面：169-171页
核心收录：
学科分类：0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0703[理学-化学] 0702[理学-物理学]
基 金：supported by the Grant Agency of the Czech Republic supported by Ministry of Education, Youth, and Sports of the Czech Republic
主 题：Magnetic modification Magnetic separation Powdered material Magnetic iron oxide Microwave assisted synthesis
摘 要：A simple method for the magnetic modification of various types of powdered agglomerate forming dia- magnetic materials was developed. Magnetic iron oxide particles were prepared from ferrous sulfate by microwave assisted synthesis. A suspension of the magnetic particles in water soluble organic solvent （methanol, ethanol, propanol, isopropyl alcohol, or acetone） was mixed with the material to be modified and then completely dried at elevated temperature. The magnetically modified materials were found to be stable in water suspension at least for 2 months.