Treatment of fir wood with chitosan and polyethylene glycol

作     者：Zahra Nowrouzi Behbood Mohebby Habibollah Younesi 

作者机构：Tarbiat Modares University Noor Iran 

出 版 物：《Journal of Forestry Research》 (林业研究（英文版）)

年 卷 期：2016年第27卷第4期

页      面：959-966页

核心收录：

学科分类：0830[工学-环境科学与工程（可授工学、理学、农学学位）] 082902[工学-木材科学与技术] 0907[农学-林学] 08[工学] 0829[工学-林业工程] 0901[农学-作物学] 

主　　题：chitosan swelling glycol polyethylene chemicals leaching dried prior chitin fixation 

摘      要：Chitosan is a natural biopolymer, derived from chitin, which is used for wood modification. Polyethylene glycol（PEG） was reacted with wood to provide possible fixation of the chitosan to wood. Wood blocks were treated with chitosan and PEG, as well as pre-treatment with the PEG at different temperatures and further reaction with the chitosan. The samples were soaked in water to study leaching of the chemicals, water absorption, swelling, as well as anti-swelling efficiency. Any prior reaction of the wood with PEG provided better reaction to the *** was increased after the treatment of the wood with PEG. Swelling was reduced in the PEG-treated wood blocks as well as the pre-treated samples. Chitosan was not able to protect wood against water penetration： the treated samples showed more water absorption and ***, pre-treatment of the samples decreased swelling in the wood, and the density was not noticeably affected by the treatments. Heating during the treatment caused more reduction in swelling for PEG–chitosan treated samples.