EFFECT OF ALLOYING ELEMENTS ON SENSITIVITY TO ENVIRONMENTAL EMBRITTLEMENT OF L1_2 INTERMETALLICS

作     者：X.J.Wan, X.Y.Cheng and Y.X.Chen Materials Research Institute, Shanghai University, Shanghai 200072, China 

出 版 物：《中国有色金属学会会刊：英文版》 (Transactions of Nonferrous Metals Society of China)

年 卷 期：1999年第9卷第S1期

页      面：117-124页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：L1 2 intermetallics environmental embrittlement hydrogen diffusivity grain boundary segregation 

摘      要：The effect of Zr doping in Ni 3Al and B doping in Co 3Ti intermetallics on the sensitivity to moisture induced environmental embrittlement and on the hydrogen diffusivity was investigated. The results show that both B in Co 3Ti and Zr in Ni 3Al do not reduce the hydrogen diffusivity along the grain boundaries, therefore can not suppress the moisture induced environmental embrittlement. The above mentioned behavior of Zr in Ni 3Al and B in Co 3Ti is attributed to the fact that Zr and B are not segregated on the grain boundaries.