Simple preparation of C(CS)/g-C_(3)N_(4)/Co carbon aerogel and its catalytic performance for ammonium perchlorate
作者机构:State Key Laboratory of Environment-friendly Energy MaterialsSchool of Materials Science and EngineeringSouthwest University of Science and TechnologyMianyang621010China
出 版 物:《Defence Technology(防务技术)》 (Defence Technology)
年 卷 期:2024年第33卷第3期
页 面:186-196页
核心收录:
学科分类:08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程(可授工学、理学学位)]
基 金:the financial support received from the Natural Science Foundation of China(21875192) Outstanding Youth Science and Technology Talents Program of Sichuan(no.19JCQN0085) Open Project of State Key Laboratory of Environment-friendly Energy Materials(Southwest University of Science and Technology,No.22fksy18)
主 题:g-C_(3)N_(4) Chitosan Co Ammonium perchlorate Pyrolysis kinetics
摘 要:Biomass chitosan(CS)was used as a template,graphitic phase carbon nitride(g-C_(3)N_(4))with high nitrogen content and certain catalytic activity was used as a dopant,and nano-transition metal cobalt(Co)was used as a catalytic center *** carbon aerogel(C(CS)/g-C_(3)N_(4)/Co)with a three-dimensional network-like structure was prepared by assembling the three materials through experimental operations such as freeze-drying and high-temperature *** was demonstrated by scanning and transmission characterization that the CS in the carbon aerogel could provide more active sites for the cobalt nanoparticles,and the doping of graphite-phase carbon nitride as a template dispersed the cobalt nanoparticles and changed the conductivity of the *** investigate the catalytic effect of carbon aerogel on ammonium perchlorate(AP),it was investigated by differential thermal analyzer and TG thermal *** carbon aerogel was very effective in catalyzing AP,and the 10 wt% content of the catalyst reduced the AP pyrolysis peak from 703.9 to 595.5 *** to further investigate the synergistic effect of the three materials,further carbon aerogels such as C(CS)/Co,g-C_(3)N_(4)/Co were prepared and applied to catalyze AP,and the same ratio reduced the AP pyrolysis peak by 98.1℃ and 97.7℃.This result indicates a synergistic effect of the assembly of the three materials.