高压物理学报 2007年第3期21卷 237-241页

作者：李雪飞张剑沈龙海杨大鹏崔启良邹广田吉林大学超硬材料国家重点实验室

以三聚氰胺和氧化硼为原料,利用真空热处理和高温高压技术,对bcn化合物的形成及结构进行了研究。在真空条件下,原料经1 100 K热处理得到非晶bcn的前驱物,将前驱物在5.0 GPa1、500 K条件下高温高压热处理30 min,合成出了单相的六角bcn晶... 详细信息

以三聚氰胺和氧化硼为原料,利用真空热处理和高温高压技术,对bcn化合物的形成及结构进行了研究。在真空条件下,原料经1 100 K热处理得到非晶bcn的前驱物,将前驱物在5.0 GPa1、500 K条件下高温高压热处理30 min,合成出了单相的六角bcn晶体。采用Materials Studio软件的Reflex模块对样品的X射线衍射图谱进行分析,结果表明,得到的样品为纯的六角相,晶格常数为a=0.250 5 nm,c=0.665 9 nm。对样品进行了透射电镜(TEM)分析,得到了样品的形貌和电子衍射,同样证实了样品为六角bcn晶体,晶粒尺寸约200 nm。对样品进行了XPS表征,确定了样品中存在C—C、C—N、C—B、N—B键,表明B、C、N三元素之间达到了原子级化合,样品的组分含量通过EDX进行标定。

关键词：高温高压 h-bcn 前驱物

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Synthesis of hexagonal Boron Carbonitride without Nitrogen Void Defects

引用

Materials Sciences and Applications 2015年第5期6卷 353-359页

作者： Md. Abdul Mannan Yuji Baba Tetsuya Kida Masamitsu Nagano hideyuki Noguchi Department of Chemistry University of Rajshahi Rajshahi Bangladesh Synchrotron Radiation Research Unit Quantum Beam Science Directorate Japan Atomic Energy Agency Ibaraki-ken Japan Sector of Fukushima Research and Development Japan Atomic Energy Agency Fukushima-shi Japan Department of Chemistry and Applied Chemistry Saga University Honjyo Japan

The synthesis and structure of hexagonal boron carbonitride (h-bcn) film on polycrystalline diamond surface were reported. Polycrystalline diamond and/or diamond-like carbon were first fabricated on Si (100) and then diamond like carbon was used as substrate. The deposition was performed by radio frequency plasma enhanced chemical vapor deposition. In order to reduce the content of nitrogen void defects, the deposition was performed at the high temperature of 950°C under the working pressure of 2.6 Pa. The typical sample with atomic composition of B31 C37 N26 O6 in the h-bcn lattice was characterized by X-ray photoelectron spectroscopy. The fine structure of the film was studied by near-edge X-ray absorption fine structure (NEXAFS) measurements. The B K-edge and N K-edge of NEXAFS spectra revealed that the synthesized h-bcn film had the ideal honeycomb- like BN3 configuration without nitrogen void defects.

关键词： h-bcn Defect Chemical Vapor Deposition XPS NEXAFS

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

hexagonal Nano-Crystalline bcn Films Grown on Si (100) Substrate Studied by X-Ray Absorption Spectroscopy

引用

Materials Sciences and Applications 2013年第5期4卷 11-19页

作者： Md. Abdul Mannan Yuji Baba Norie hirao Tetsuya Kida Masamitsu Nagano hideyuki Noguchi Department of Chemistry and Applied Chemistry Faculty of Science and Engineering Saga University Saga Japan Department of Chemistry and Applied Chemistry Faculty of Science and Engineering Saga University Saga Japan Synchrotron Radiation Research Unit Quantum Beam Science Directorate Japan Atomic Energy Agency Ibaraki Japan Synchrotron Radiation Research Unit Quantum Beam Science Directorate Japan Atomic Energy Agency Ibaraki Japan

hexagonal nano-crystalline boron carbonitride (h-bcn) films grown on Si (100) substrate have been precisely investigated. The films were synthesized by radio frequency plasma enhanced chemical vapor deposition using tris-dimethylamino borane as a single-source molecular precursor. The deposition was performed by setting RF power at 400 - 800 W. The reaction pressure was at 2.6 Pa and the substrate temperature was recorded at 700°C - 800°C. Formation of the nano-crystalline h-bcn compound has been confirmed by X-ray diffraction analysis. The diffraction peaks at 26.3° together with a small unknown peak at 29.2° were elucidated due to the formation of an h-bcn structure. The films composed of B, C, and N atoms with different B-N, B-C, C-N chemical bonds in forming the sp2-bcn atomic configuration studied by X-ray photoelectron spectroscopy. Orientation and local structures of the h-bcn hybrid were studied by near-edge X-ray absorption fine structure (NEXAFS) measurements. The dominant presence of p* and s* resonance peaks of the sp2-hybrid orbitals in the B K-edge NEXAFS spectra revealed the formation of the sp2-bcn configuration around B atoms like-BN3 in h-BN. The orientation was suggested on the basis of the polarization dependence of B K-edge and N K-edge of the NEXAFS spectra.

关键词： Nano-Crystalline h-bcn Films Synchrotron Radiation XPS NEXAFS Orientation

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

六方硼碳氮制备方法的研究进展

引用

材料导报 2015年第15期29卷 44-51页

作者：康越原博马天楚增勇黄献聪总后勤部军需装备研究所北京100010 国防科学技术大学理学院长沙410073

B-C-N材料的提出是由于氮化硼和碳材料具有特殊的优异性能,通过对不同结构B-C-N材料的研究发现,组成结构的差异导致其物理化学性能发生很大变化。其中,h-bcn由于其禁带宽度和半导体特性可调而尤为引人关注。h-bcn有平面和层状两种结构,... 详细信息

B-C-N材料的提出是由于氮化硼和碳材料具有特殊的优异性能,通过对不同结构B-C-N材料的研究发现,组成结构的差异导致其物理化学性能发生很大变化。其中,h-bcn由于其禁带宽度和半导体特性可调而尤为引人关注。h-bcn有平面和层状两种结构,基于目前两种结构的h-bcn制备方法的最新研究进展,简述了材料的结构、生长机理、性质和应用前景,分析了反应原料、温度和时间对h-bcn形成的影响,最后介绍了h-bcn亟待解决的问题和发展方向。

关键词： h-bcn 石墨烯层状结构平面结构

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：