Effect of annealing temperature on microstructure and mechanical properties of mg-zn-zr-nd alloy with large final rolling deformation

引用

Journal of Central South University 2024年第6期31卷 1774-1789页

作者： ZHANG Jin-hai NIE Kai-bo ZHANG Jin-hua DENG Kun-kun LIU Zhi-long College of Materials Science and Engineering Taiyuan University of TechnologyTaiyuan 030024China State Key Laboratory of High-end Compressor and System Technology Hefei 230031China

In this study,the mg-3zn-0.5zr-χnd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was *** rolled mg-3zn-0.5zr-0.6nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both *** mechanical properties for the mg-3zn-0.5zr-0.6nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening *** annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the ***,the addition of nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.

关键词： mg-zn-zr-nd alloy large final rolling deformation annealing temperatures microstructures mechanical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Mechanical properties, biodegradability and cytocompatibility of biodegradable mg-zn-zr-nd/Y alloys

引用

Journal of Materials Science & Technology 2020年第12期47卷 190-201页

作者： Shi Jin Dan Zhang Xiaopeng Lu Yang Zhang Lili Tan Ying Liu Qiang Wang School and Hospital of Stomatology China Medical UniversityShenyang 110001China Liaoning Provincial Key Laboratory of Oral Diseases Shenyang 110001China Institute of Metal Research Chinese Academy of SciencesShenyang 110016China Shenyang National Laboratory for Materials Science Northeastern UniversityShenyang 110819China School of Stomatology Jiamusi UniversityJiamusi 154007China

Biodegradable magnesium alloys have been turned out to be a promising candidate for orthopedic *** this study,the mechanical properties,degradation behaviorand cytocompatibility of mgzn-zr-nd and mg-zn-zr-Y alloys were studied in comparison with pure *** tests showed that the strength and ductility of mg-zn-zr-nd and mg-zn-zr-Y alloys were *** corrosion resistance analyzed by electrochemical test and immersion test in alpha modified eagle(α-MEM) medium with 10% fetal bovine serum(FBS) revealed the degradation of mg-zn-zr-nd and mg-zn-zr-Y alloys were faster than pure mg at an early stage but slowed down after long time *** metal ion concentrations were consistent with the corrosion ***-zn-zr-nd alloy shows better mechanical properties than pure mg and better corrosion resistance than mg-zn-zr-Y *** direct and indirect in vitro tests with MC3 T3-E1 cells demonstrate that mg-zn-zr-nd shows the best cytocompatibility and *** results suggest that mg-zn-zr-nd alloy shows an ideal combination of mechanical,corrosive and biological *** summary,these results implying the mg-zn-zr-nd alloy has great potential to benefit the future development of orthopedic applications.

关键词： Magnesium mg-zn-zr-nd alloy mg-zn-zr-Y alloy Biodegradable implant Biocompatibility

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Non-destructive corrosion study on a magnesium alloy with mechanical properties tailored for biodegradable cardiovascular stent applications

引用

Journal of Materials Science & Technology 2021年第7期66卷 128-138页

作者： Changhong Cai Marta M.Alves Renbo Song Yongjin Wang Jingyuan Li School of Materials Science and Engineering University of Science and Technology BeijingBeijing100083China Centro de Qufmica Estrutural Instituto Superior TecnicoUniversidade de LisboaAv.Rovisco Pais1049-001LisboaPortugal

Anmg-2zn-0.6zr-0.6nd alloy for biodegradable cardiovascular stent applications was prepared through indirect extrusion. The alloy exhibited a superior combination of tensile yield strength(TYS), ultimate tensile strength(UTS) and elongation(EL) of about 269 MPa, 298 MPa and 25.6 %, respectively. In addition,the non-destructive electrochemical frequency modulation(EFM) technique was used for the first time to investigate the corrosion behavior of mg alloys combined with electrochemical impedance spectroscopy(EIS) in Dulbecco’s Modified Eagle’s Medium(DMEM) and in Hank’s solution. Compared with the corrosion rate of 0.07 mm/year in Hank’s solution, lower corrosion rate of 0.03 mm/year was achieved in DMEM. The significant differences between the corrosion rate trends were discussed and related with the composition of the corrosion layer formed. Depending on the biomimetic fluids tested, different corrosion products were precipitated on the alloy’s surface: a compact and homogeneous layer of mg_(x)Ca_(y)(PO_(4))_(z) and zn(OH)_(2) and organic compounds was formed in DMEM, whereas a partial coverage of mg_(x)Ca_(y)(PO_(4))_(z) and zn(OH)_(2) was formed in Hank’s solution.

关键词： mg-zn-zr-nd alloy Mechanical property Corrosion EIS EFM

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：