Interface evolution of Cu-Ni-Si/Al-Mg-Si clad composite wires after annealing

Rare Metals 2020年第12期39卷 1419-1424页

作者： Zhen Yang Xu-Jun Mi Xue Feng Hao-Feng Xie Li-Jun Peng Guo-Jie Huang Yan-Feng Li Xiang-Qian Yin Key Laboratory of Nonferrous Metals and Processes GRIMAT Engineering Institute Co.LtdBeijing 101400China

Interface micros tructures of Cu-Ni-Si/Al-MgSi clad composite wires during isothermal annealing from 623 to 773 K were *** composite wires were fabricated by a drawing *** evolution of intermetallic compounds(IMCs)was analyzed.A continuous IMCs layer forms only after annealing for 1 min,which may be due to more IMCs nucleation points generated by deep drawing *** consist of Al_(4)Cu_(9),AlCu and Al_(2)Cu identified by energy-dispersive spectroscopy(EDS)and transmission electron microscopy(TEM).The growth activation energies of total IMCs,Al_(2)Cu,AlCu and Al_(4)Cu_(9),are 98.8,69.4,101.3 and 137.1 kJ·mol^(-1),*** higher growth activation energy of Al_(4)Cu_(9)results in the higher growth rate under high ***,the average interdiffusion coefficient for each IMC calculated by Wagner method shows that interdiffusion in Al_(2)Cu and AlCu is more active than that in Al_(4)Cu_(9).The higher growth rate of Al_(4)Cu_(9)may be caused by the long concentration range.

关键词： Intermetallic compounds clad composite wires Diffusion Activation energy

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：