ZnCl_2-assisted Synthesis of ZnSe Polycrystal

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2012年第4期28卷 373-378页

作者： Changyou Liu Tao Wang gangqiang zha Zhi Gu Wanqi Jie State Key Laboratory of Solidification Processing School of Materials Science and EngineeringNorthwestern Polytechnical UniversityXi'an 710072China

A chemical-assisted element direct-reaction method is developed to synthesize ZnSe compound semiconductor material at a relatively low temperature （-1000 ℃）. ZnSe polycrystal was obtained in the closed-tube systems with Zn-Se, Zn-Se-Zn（NHa）2CI2, ZnoSe-NH4CI and Zn-Se-ZnCI2. The as-synthesized samples were tested by X-ray diffraction （XRD）, thermogravimetric analysis （TGA） and analyzed by thermodynamic numerical method. The results demonstrate that the synthesis efficiency is higher than 99.96% for Zn-Se-ZnCl2 system at around 1000 ℃ for 3 weeks. It also exhibits that not only temperature, but also low apparent ratio of volume and surface area of the source materials and higher ZnCl2 content are required to achieve high synthesis efficiency. A SeCI transporting reaction synthesis process is proposed based on the thermodynamic analysis.

关键词： Crystallites Growth from vapor Zinc compounds Semiconducting II-VI materials

The analysis of X-ray response of CdZnTe detectors

在线全文

学校读者我要写书评

暂无评论

Science China(Technological Sciences) 2012年第8期55卷 2295-2299页

作者： zha gangqiang XIANG Hang LIU Ting XU YaDong WANG Tao JIE WanQi State Key Laboratory of Solidification Processing Northwestern Polytechnical UniversityXi'an 710072China

CdZnTe is an excellent material candidate for high efficiency,high-resolution room-temperature nuclear radiation detectors,and the CdZnTe detectors are being widely used in medicine,industry,safeguard and scientific X-ray and γ-ray imaging and spectroscopic *** this work,three CdZnTe planar detectors with different grades,named CZT-1,CZT-2 and CZT-3,respectively,were *** the effects of mobility,lifetime and de-trapping time on the performance of CdZnTe planar detector,such as the energy resolution,charge collection efficiency and peak to valley ratio,were *** charge collection efficiency depends on the product of carrier mobility and lifetime,which has a great effect on the energy resolution of detector when the efficiency is less than 90%.The de-trapping time of carriers in deep levels should be responsible for the peak to valley ratio and "polarization".

关键词： CdZnTe radiation detector energy spectra carrier transport

Design and technology review of the solar X-ray detector onboard the Macao Science Satellite-1B

在线全文

学校读者我要写书评

暂无评论

Science China(Technological Sciences) 2024年第11期67卷 3365-3380页

作者： ZUO FuChang SHI YongQiang CHEN JianWu zhaNG XiaoPing FU WeiChun CHANG Ye GAI FangQin LIU SiYuan XIONG Yan zhaNG HaiLi SUN Yan WANG Li ZHENG Ran LI LianSheng MEI ZhiWu HUANG He zha gangqiang zhaNG KeKe Space Optoelectronic Measurement and Perception Lab. Beijing Institute of Control EngineeringBeijing 100190China State Key Laboratory of Lunar and Planetary Sciences Macao University of Science and TechnologyMacao 999078China School of Astronautics Northwestern Polytechnical UniversityXi’an 710072China Key Laboratory of Radiation Detection Materials and Devices Northwestern Polytechnical UniversityXi’an 710072China Research and Development Institute of Northwestern Polytechnical University in Shenzhen Shenzhen 518063China

On May 21,2023,the Macao Science Satellite-1B(MSS-1B),a low-inclination,low-latitude,and high-precision scientific exploration satellite for geomagnetic fields and space environments,was successfully *** solar X-ray detector(SXD),one of the two major scientific payloads onboard the MSS-1B,has obtained a large amount of solar X-ray radiation data,which reveals the distribution law of the magnetic field in the low Earth orbit,as well as the coupling law of the Earth's magnetic field and the solar radiation and energy particle ***,the overall design of the multi-detection-unit,broad-energy-range,small-volume,and low-power SXD was implemented to achieve the scientific objectives of the ***,the technical indicators of the instrument were decomposed into various components,and the key technologies,such as collimator,processing circuit,thermal,and payload dataset designs,were ***,the backgrounds,including electronic noise,cosmic diffuse X-ray background,and high-energy background in the Earth's radiation belts in and out of the field of view,were analyzed for the ***,the ground calibrations of the energy response,detection efficiency,and temperature-dependent peak drift of the SXD flight model were ***,the in-orbit temperature,energy spectrum data,background,and solar flare process observation of the instrument in the in-orbit test stage are presented,verifying the instrument design,analysis,and ground calibration,providing a foundation for obtaining accurate solar X-ray radiation data,and achieving the scientific objectives of the satellite.

关键词： Macao Science Satellite-1B solar X-ray detector design and development solar flare technology review

CsPbBr3单晶薄膜制备及其X射线探测性能研究

在线全文

学校读者我要写书评

暂无评论

人工晶体学报 2021年第10期50卷 1900-1906页

作者：张欣雷王涛查钢强西北工业大学辐射探测材料与器件工信部重点实验室西北工业大学深圳研究院

X射线探测在医疗、工业无损检测、国土安全等领域具有重要意义。制备高灵敏度的X射线探测器可以降低X射线剂量,在医疗和安检中至关重要。本文系统研究了采用空间限域法制备的高质量CsPbBr3单晶薄膜,并用该薄膜制备出了性能良好的X射线... 详细信息

X射线探测在医疗、工业无损检测、国土安全等领域具有重要意义。制备高灵敏度的X射线探测器可以降低X射线剂量,在医疗和安检中至关重要。本文系统研究了采用空间限域法制备的高质量CsPbBr3单晶薄膜,并用该薄膜制备出了性能良好的X射线探测器。借助偏光显微镜、扫描电子显微镜及其配备的能谱系统和背散射电子衍射系统对薄膜的形貌、厚度、成分和取向进行了分析。研究发现所制备的单晶薄膜表面平整、光滑,元素分布均匀,晶体取向均一。利用该薄膜制备的探测器具有较高电阻率(约7.23×10~8 W·cm)和极高的灵敏度(约2 610μC·Gy-1·cm-2)。

关键词： CsPbBr3 钙钛矿单晶薄膜 X射线探测高灵敏度空间限域法

含氧空位单斜相HfO_2电子结构和光学性质的第一性原理研究

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

稀有金属材料与工程 2013年第8期42卷 1576-1580页

作者：査钢强汤三奇谭婷婷西北工业大学凝固技术国家重点实验室陕西西安710072

采用基于密度泛函理论的平面波超软赝势方法对含氧空位单斜相HfO2的电子结构和光学性质进行了计算。计算结果表明,氧空位缺陷的存在使得HfO2带隙中出现了缺陷态,主要由最近邻Hf原子的5d态组成。随后,结合计算的电子态密度分析了氧空位对... 详细信息

采用基于密度泛函理论的平面波超软赝势方法对含氧空位单斜相HfO2的电子结构和光学性质进行了计算。计算结果表明,氧空位缺陷的存在使得HfO2带隙中出现了缺陷态,主要由最近邻Hf原子的5d态组成。随后,结合计算的电子态密度分析了氧空位对HfO2材料介电常数和吸收系数的影响。氧空位存在时,在380～220 nm的紫外波段内出现了较弱的吸收峰。

关键词：单斜相HfO2 氧空位电子结构光学性质

热处理参数对TA15钛合金静态球化显微组织及动力学的影响

在线全文

学校读者我要写书评

暂无评论

金属热处理 2018年第6期43卷 79-83页

作者：王蕊宁孙润军查刚强西安工程大学纺织科学与工程学院陕西西安710048 西北工业大学材料学院陕西西安710072

首先对TA15合金进行了变形量分别为60%,75%和90%的轧制,然后在800、850和930℃分别进行了15、30、45和60 min的热处理试验。利用OM、SEM和Image-pro Plus 5.0等手段研究了TA15合金在不同状态下的显微组织和静态球化行为。结果表明：静... 详细信息

首先对TA15合金进行了变形量分别为60%,75%和90%的轧制,然后在800、850和930℃分别进行了15、30、45和60 min的热处理试验。利用OM、SEM和Image-pro Plus 5.0等手段研究了TA15合金在不同状态下的显微组织和静态球化行为。结果表明：静态球化过程中晶内针状次生α相断裂及球化行为比晶界α相更易于发生;TA15合金静态球化行为的发生对温度敏感,850℃获得球化比例可增加至95%,930℃球化率不变但晶粒长大明显,晶界清晰化。通过JMAK方程对TA15合金的静态球化动力学过程模拟,发现温度、时间对球化率的影响规律为随热处理温度和原始变形量的增加,球化率随热处理时间增加但上升趋势降低。

关键词： TA15钛合金静态球化显微组织动力学

在线全文

学校读者我要写书评

暂无评论

EPG 535光刻胶氧离子刻蚀工艺的研究

压电与声光 2011年第4期33卷 523-526页

作者：任洁傅莉孙玉宝査钢强西北工业大学凝固技术国家重点实验室陕西西安710072

采用反应离子刻蚀(RIE)技术,对EPG 535光刻胶和碲锌镉(CZT)基体刻蚀工艺进行研究,采用原子力显微镜(AFM)法测试CZT基体刻蚀前后的表面质量,探讨了EPG 535光刻胶刻蚀速率和CZT基体表面粗糙度的影响因素。结果表明,当RF功率为60 W、氧气... 详细信息

采用反应离子刻蚀(RIE)技术,对EPG 535光刻胶和碲锌镉(CZT)基体刻蚀工艺进行研究,采用原子力显微镜(AFM)法测试CZT基体刻蚀前后的表面质量,探讨了EPG 535光刻胶刻蚀速率和CZT基体表面粗糙度的影响因素。结果表明,当RF功率为60 W、氧气气压为1.30 Pa、氧气流量为40 cm3/min,光刻胶达到最大刻蚀速率;随着RF功率降低,刻蚀后CZT基体的表面粗糙度降低。实验优化的刻蚀参数为:RF功率40 W、氧气气压1.30 Pa、氧气流量40 cm3/min。

关键词：氧气反应离子刻蚀(RIE) EPG 535光刻胶碲锌镉晶片表面粗糙度刻蚀速率

温度对碲锌镉光子计数探测器计数性能的影响及机理研究

在线全文

学校读者我要写书评

暂无评论

红外与激光工程 2019年第10期48卷 240-245页

作者：李颖锐吴森郭玉席守智符旭查钢强介万奇西北工业大学凝固技术国家重点实验室辐射探测材料与器件工信部重点实验室陕西西安710071 陕西迪泰克新材料有限公司陕西西安710071

基于线阵光子计数探测器模块,实现了碲锌镉探测器的光子计数应用。研究了大剂量X射线下碲锌镉探测器的计数性能,发现碲锌镉光子计数探测器根据其典型计数性能可分为两类:C1,C2。分析了这两类典型的光子计数探测器的计数性能与X射线能谱... 详细信息

基于线阵光子计数探测器模块,实现了碲锌镉探测器的光子计数应用。研究了大剂量X射线下碲锌镉探测器的计数性能,发现碲锌镉光子计数探测器根据其典型计数性能可分为两类:C1,C2。分析了这两类典型的光子计数探测器的计数性能与X射线能谱响应特性、前放脉冲信号上升时间以及碲锌镉探测器缺陷水平的内在联系,在此基础上研究了温度对C2类碲锌镉光子计数探测器计数性能的影响规律,升高温度可以抑制探测器的极化失效,提高计数率,且当温度升高至33℃时,探测器计数性能可得到显著改善。最后利用线阵光子计数探测器模块,获得了不同温度下C2类碲锌镉光子计数探测器的多能区成像结果,升高温度可以显著增加其图像衬度,提高成像质量。该研究为通过控制外部条件提高碲锌镉光子计数探测器性能提供了有效手段。

关键词：碲锌镉光子计数极化效应温度多能区成像

CdZnTe晶体(111)面摇摆曲线不唯一现象研究

在线全文

学校读者我要写书评

暂无评论

Journal of Semiconductors 2007年第Z1期28卷 80-83页

作者：曾冬梅王涛李强查钢强介万奇西北工业大学材料学院西安710072 西北工业大学材料学院西安710072 西北工业大学材料学院西安710072 西北工业大学材料学院西安710072 西北工业大学材料学院西安710072

CdZnTe晶体通常利用其(333)晶面的X射线衍射摇摆曲线来检测(111)晶面的结晶质量.本文根据CdZnTe晶体(333)面摇摆曲线实验结果,首次提出了CdZnTe晶体摇摆曲线的不唯一现象.摇摆曲线的这种不唯一现象是样品绕(111)面法线方向旋转360.过程... 详细信息

CdZnTe晶体通常利用其(333)晶面的X射线衍射摇摆曲线来检测(111)晶面的结晶质量.本文根据CdZnTe晶体(333)面摇摆曲线实验结果,首次提出了CdZnTe晶体摇摆曲线的不唯一现象.摇摆曲线的这种不唯一现象是样品绕(111)面法线方向旋转360.过程中,晶体的(333)面和(333)面在同一衍射几何中都发生了布拉格衍射,优化扫描后得出两个摇摆曲线.分析了CdZnTe晶体(333)面和(-333)面对X射线散射能力,得出CdZnTe晶体(333)面的衍射强度小于(-333)面的衍射强度,所以在同等实验条件下,对同一CdZnTe晶片(333)面的摇摆曲线的强度比(333)面摇摆曲线的强度低.

关键词： CdZnTe 不唯一现象摇摆曲线结构因子