Black liquor is obtained as a by-product of the pulping process,which is used to convert biomass into pulp by removing lignin,hemicelluloses and other extractives from wood to free cellulose fibers.Lignin represents a...
详细信息
Black liquor is obtained as a by-product of the pulping process,which is used to convert biomass into pulp by removing lignin,hemicelluloses and other extractives from wood to free cellulose fibers.Lignin represents a major constituent in black liquor,with quantities varying from 20%to 30%,of which a very low share is used for manufacturing value-added products,while the rest is mainly burned for energy purposes,thus underestimating its great potential as a raw material.Therefore,it is essential to establish new isolation and extraction methods to increase lignin valorization in the development of bio-based chemicals.The aim of this research work was to determine the effect of KOH or ethanol concentration as an isolation agent on lignin yields and the chemical characteristics of lignin isolated from formacell black liquor of oil palm empty fruit bunch(OPEFB).Isolation of lignin was carried out using KOH with various concentrations ranging from 5%to 15%(w/v).Ethanol was also used to precipitate lignin from black liquor at concentrations varying from 5%to 30%(v/v).The results obtained showed that the addition of KOH solution at 12.5%and 15%concentrations resulted in better lignin yield and chemical properties of lignin,i.e.,pH values of 3.86 and 4.27,lignin yield of 12.78%and 14.95%,methoxyl content of 11.33%and 10.13%,and lignin equivalent weights of 476.25 and 427.03,respectively.Due to its phenolic structure and rich functional groups that are favorable for modifications,lignin has the potential to be used as a green additive in the development of advanced biocomposite products in various applications to replace current fossil fuel-based material,ranging from fillers,fire retardants,formaldehyde scavengers,carbon fibers,aerogels,and wood adhesives.
The aim of this research work was to evaluate the potential of using renewable natural feedstock,i.e.,Jatropha curcas oil(JCO)for the synthesis of non-isocyanate polyurethane(NIPU)resin for wood composite applications...
详细信息
The aim of this research work was to evaluate the potential of using renewable natural feedstock,i.e.,Jatropha curcas oil(JCO)for the synthesis of non-isocyanate polyurethane(NIPU)resin for wood composite applications.Commercial polyurethane(PU)is synthesized through a polycondensation reaction between isocyanate and poly-ol.However,utilizing toxic and unsustainable isocyanates for obtaining PU could contribute to negative impacts on the environment and human health.Therefore,the development of PU from eco-friendly and sustainable resources without the isocyanate route is required.In this work,tetra-n-butyl ammonium bromide was used as the activator to open the epoxy ring with 3-Aminopropyltriethoxisylane as a catalyst to yield urethane of JCO(UJCO).The UJCO were characterized by Fourier Transform Infra-Red spectroscopy(FTIR)and their oxirane,and hydroxyl values were measured.The result showed that a decrease in oxirane value was found while the hydroxyl value was increased during the time,confirming that the urethane group was formed.The presence of functional groups in FTIR spectra at wave numbers 1732.08,1562.34,and 3348.42 cm^(−1) indicates the functional groups of C=O(urethane carbonyl),–NH,and–OH,respectively confirmed this finding.The potential applications of NIPU in the wood composite were also outlined.
暂无评论