Frontiers of Environmental Science & Engineering 2024年第5期18卷 43-55页

作者： Xian Zhou Zhengfu Zhang hui yang School of Materials Science and Engineering Kunming University of Science and TechnologyKunming650093China Kunming Metallurgical Research Institute Co. Ltd.Kunming650031China

Tin mine tailings(TMT)and fuming slag(FS)contain many heavy metals(As,Cr,Cu,Zn and Mn)that cause severe pollution to the ***,geopolymers were prepared using TMT,FS and flue gas desulfurization gypsum(FGDG)to immobilize heavy metals,and their compressive strength and heavy metal leaching toxicity were *** was first determined that T4F5(TMT:FS=4:5)sample exhibited the highest compressive strength(7.83 MPa).T4F5 achieved 95%immobilization efficiency for As and Cr,and nearly 100%for Cu,Zn and Mn,showing good immobilization performance.A series of characterization analyses showed that heavy metal cations can balance the charge in the geopolymer and replace Al in the geopolymer structure to form covalent *** addition,about 2%–20%of heavy metal Fe was immobilized in hydration products,heavy metal hydroxides and non-bridging Si–O and Al–O coordination with silica-aluminate ***_(3)^(3−) was oxidized into AsO_(4)^(3−),which may form Ca–As or Fe–As ***_(2)O_(7)^(2−)was converted to CrO_(4)^(2−)under alkaline environment and then combined with OH−to form Cr(OH)3 ***^(2+)may react directly with dissolved silicate to form Mn_(2)SiO_(4) and also form Mn(OH)_(2) *** unstable Mn(OH)_(2) can be further oxidized to MnO_(2).The heavy metal cations were immobilized in the silicoaluminate lattice,while the anions tended to form insoluble *** results may benefit the industry and government for better handling of TMT,FS and solid wastes containing the abovementioned five heavy metals.

关键词： Heavy metals Cementitious materials Tin tailings Stabilization/solidification Redox

Simultaneously enhancing erosion and compression resistance:designing AlCoCrFeNi high-entropy alloy strengthened Ag-based contacts

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第9期43卷 4476-4492页

作者： Xiao-yang Xue Zhe Wang hui-ling Nie Zhao Yuan Jun Wang Chang-Hu Xu Kai Wen Cong-Hao Yu School of Materials Science and Engineering Xi’an Polytechnic UniversityXi’an 710048China School of Physics Xi’an Jiaotong UniversityXi’an 710049China Key Laboratory of Pulsed Power Technology School of Electrical and Electronic EngineeringHuazhong University of Science and TechnologyWuhan 430074China State Key Laboratory of Advanced Electromagnetic Engineering and Technology School of Electrical and Electronic EngineeringHuazhong University of Science and TechnologyWuhan 430074China

Designing microstructures and unveiling dynamic erosion mechanisms remain important challenges for Ag-based *** simultaneously enhance erosion and compression resistance,an Al Co Cr Fe Ni high-entropy alloy(HEA)is introduced into Ag-based materials to fabricate novel Ag-HEA contacts with island-and skeletonrestricted *** arc erosion experimental results reveal that the skeleton-restricted HEA microstructure is the key factor in reducing the hill and crater morphologies of the contact surface,effectively delaying material transfer between the movable and stationary *** molten bridge evolution and compressive deformation behavior of Ag-HEA contacts with various microstructures are investigated using molecular dynamics(MD)*** results indicate that the constraint of Ag atom diffusion in the molten pool and the involvement of HEA atoms in the molten bridge are the primary mechanisms for improving erosion *** skeleton-restricted HEA microstructure reduces the total energy and structural stability of the molten bridge system and promotes its fracture and ***,the synergistic effect of the twin and Lomerz–Cottrell lock structures can hinder dislocation glide,generating dispersed and small-area stacking faults in the Ag matrix and mitigating the concentration of shear ***,the skeleton-restricted HEA microstructure contributes positively to compression *** study presents a novel approach to designing Ag-based contacts.

关键词： Electrical contact materials High entropy alloys Arc erosion Molecular dynamics Microstructures

Exploring the potential of constructing a hybrid supercapacitor with FeCoNi-LDH porous material containing oxygen vacancies for high-performance energy storage applications

在线全文

学校读者我要写书评

暂无评论

Nano Research 2024年第9期17卷 8134-8144页

作者： Jihao Su ling yang Dengbin Yu Shaojun Dong State Key Laboratory of Electroanalytical Chemistry Changchun Institute of Applied ChemistryChinese Academy of SciencesChangchun 130022China College of Chemistry Jilin UniversityChangchun 130022China University of Science and Technology of China Hefei 230026China

A significant challenge in developing high-performance hybrid supercapacitors(HSCs)is the need to reasonably construct advanced architectures that consist of various components and exhibit superior electrochemical capacitance *** FeCoNi-layered double hydroxide(FeCoNi-LDH)porous material has a specific capacitance of 1960 F·g^(-1)when used as the anode material at 1 A·g^(-1).The FeCoNi-LDH material exhibits nanoplates with a distinct spindle morphology on their *** to the combined action of the three metals and abundant oxygen vacancies,they exhibit unique rate performance and cycle *** electronic structure of LDH and the regulation of oxygen vacancy were confirmed by density functional theory(DFT)*** suggests that the strength of hydroxide can reduce the energy required for oxygen vacancy formation in FeCoNi-LDH nanosheets and enhance ion and charge transfer,as well as electrolyte adsorption on the electrode *** FeCoNi-LDH//activated carbon(AC)HSC has an energy density of 53.2 Wh·kg^(-1)at a power density of 800 W·kg^(-1),surpassing other devices composed of comparable materials during the same *** study made significant advances in the design and synthesis of a ternary LDH porous structure with distinct oxygen vacancies,as well as its potential application in electrochemical energy storage.

关键词： oxygen vacancy FeCoNi-layered double hydroxide(FeCoNi-LDH) theory calculation electrode material hybrid supercapacitor

Surgical resection and neoadjuvant therapy in patients with gastric cancer and ovarian metastasis: A real-world study

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

World Journal of Gastrointestinal Surgery 2024年第8期16卷 2426-2435页

作者： hui-Ping Yan Hong-Rui Lu Yu-Xia Zhang Liu yang Zhe-ling Chen School of Public Health Hangzhou Medical CollegeHangzhou 310000Zhejiang ProvinceChina Cancer Center Department of Medical OncologyZhejiang Provincial People’s Hospital(Affiliated People’s Hospital)Hangzhou 310000Zhejiang ProvinceChina Affiliated Bijie Hospital Zhejiang Provincial People’s HospitalBijie 551700Guizhou ProvinceChina

BACKGROUND Regarding when to treat gastric cancer and ovarian metastasis(GCOM)and whether to have metastatic resection surgery,there is presently debate on a global *** purpose of this research is to examine,in real-world patients with GCOM,the survival rates and efficacy of metastatic vs non-metastasized *** To investigate the survival time and efficacy of metastatic surgery and neoadjuvant therapy in patients with *** This study retrospectively analyzed the data of 41 GCOM patients admitted to Zhejiang Provincial People’s Hospital from June 2009 to July *** diagnosis of all patients was confirmed by *** primary study endpoints included overall survival(OS),ovarian survival,OS after surgery(OSAS),disease-free survival(DFS),differences in *** This study had 41 patients in *** surgical group(n=27)exhibited significantly longer median OS(mOS)and median overall months(mOM)compared to the nonoperative group(n=14)(mOS:23.0 vs 6.9 months,P=0.015;mOM:18.3 vs 3.8 months,P=0.001).However,there were no significant differences observed in mOS,mOM,median OSAS(mOSAS),and median DFS(mDFS)between patients in the surgical resection plus neoadjuvant therapy group(n=11)and those who surgical resection without neoadjuvant therapy group(n=16)(mOS:26.1 months vs 21.8 months,P=0.189;mOM:19.8 vs 15.2 months,P=0.424;mOSAS:13.9 vs 8.7 months,P=0.661,mDFS:5.1 vs 8.2 months,P=0.589).CONCLUSION Compared to the non-surgical group,the surgical group’s survival duration and efficacy are noticeably *** efficacy and survival time of the direct surgery group and the neoadjuvant therapy group did not differ significantly.

关键词： Gastric cancer Prognosis Ovarian metastasis Neoadjuvant therapy Surgery

Crystalline-amorphous M@MN_x(M=Co,Fe,Ni)encapsulated in nitrogen-doped carbon for enhanced efficient and durable hydrogen evolution reaction

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第4期43卷 1547-1556页

作者： yang yang Xiao-Chuan Duan Shao-hui Guo Xian-Ming Zhang College of Materials Science and Engineering College of ChemistryKey Laboratory of Interface Science and Engineering in Advanced MaterialsTaiyuan University of TechnologyYuci030600China

Developing earth-abundant electrocatalysts for hydrogen evolution reaction(HER)is important for the sustainable energy ***,efficient and stable heterocatalysts consisting of crystalline-amorphous M@MN_(x)(M=Co,Fe,Ni)encapsulated in N-doped carbon layers supported with N-doped graphene sheets(denoted as M@MN_(x)@NC-NG)are synthesized by facile hydrothermal reaction and nitridation *** the nitriding process,metal ions in M(tzbc)_2(H_(2)O)_4(tzbc=4-(1H-1,2,4-triazol-1-yl)benzoic acid)complexes are reduced to crystalline M cores,accompanied by the formation of amorphous MN_(x)shells;the tzbc ligands are insitu carbonized to form outermost N-doped carbon(NC)layers that connect with inner MN_(x)via M-N-C motifs inherited from the complex precursors and inhibit the transition of MN_(x)from amorphous to crystalline *** Co@CoN_(x)@NC-NG catalyst exhibits excellent HER activity with small overpotentials of 45 and 64 mV at a cathode current density of 10 mA·cm^(-2)and low Tafel slopes of 40 and 85 mV·dec^(-1)in 0.5 mol·L^(-1)H_(2)SO_4 and1.0 mol·L^(-1)KOH electrolytes,*** Co@CoN_(x)@NC-NG retains 97%of the initial overpotential after 100,000 s in both acidic and alkaline *** outstanding HER performance originates from the crystalline-amorphous Co@CoN_(x)that redistributes electrons around the heterointerfaces,facilitating the conversion process of H^(+)/H_(2)O to hydrogen and thereby promoting HER *** outermost NC layers serve as the armor of Co@CoN_(x),and graphene nanosheets act as carriers of egg-like Co@CoN_(x)@NC and conduction paths for electron shuttles,ensuring stable and continuous electrocatalytic hydrogen production.

关键词： Hydrogen evolution reaction Electrocatalysts Iron group metals Heterojunction Crystalline-amorphous structure

Adaptive composite anti-disturbance control for heavy haul trains

在线全文

学校读者我要写书评

暂无评论

Transportation Safety and Environment 2024年第1期6卷 75-82页

作者： Longsheng Chen hui yang School of Electrical and Automation Engineering East China Jiaotong UniversityNanchang 33013JiangxiChina School of Aircraft Engineering Nanchang Hangkong UniversityNanchang 330063JiangxiChina

In this paper,an adaptive composite anti-disturbance control of heavy haul trains(HHTs)is ***,the mechanical principle and characteristics of couplers are analysed and the longitudinal multi-particles nonlinear dynamic model of HHTs is established,which can satisfy that the forces of vehicles in different positions are ***,a radial basis function network(RBFNN)is employed to approximate the uncertainties of HHTs,and a nonlinear disturbance observer(NDO)is constructed to estimate the approximation error and external *** indicate and improve the approximation accuracy,a serial-parallel identification model of HHTs is constructed to generate a prediction error,and an adaptive composite anti-disturbance control scheme is developed,where the prediction error and tracking error are employed to update RBFNN weights and an auxiliary variable of ***,the feasibility and effectiveness of the proposed control scheme are demonstrated through the Lyapunov theory and simulation experiments.

关键词： heavy haul train(HHT) radial basis function neural network nonlinear disturbance observer(NDO) serial-parallel identification model composite anti-disturbance control

Recent progresses in thermal treatment of β-Ga_(2)O_(3) single crystals and devices

在线全文

学校读者我要写书评

暂无评论

International Journal of Minerals,Metallurgy and Materials 2024年第7期31卷 1659-1677页

作者： Yuchao Yan Zhu Jin hui Zhang Deren yang State Key Laboratory of Silicon and Advanced Semiconductor Materials and School of Materials Science and Engineering Zhejiang UniversityHangzhou 310027China Zhejiang Provincial Key Laboratory of Power Semiconductor Materials and Devices ZJU-Hangzhou Global Scientific and Technological Innovation CenterHangzhou 311200China

In recent years,ultra-wide bandgap β-Ga_(2)O_(3) has emerged as a fascinating semiconductor material due to its great potential in power and photoelectric *** semiconductor industrial,thermal treatment has been widely utilized as a convenient and effective approach for substrate property modulation and device ***,a thorough summary of β-Ga_(2)O_(3) substrates and devices behaviors after high-temperature treatment should be *** this review,we present the recent advances in modulating properties of β-Ga_(2)O_(3) substrates by thermal treatment,which include three major applications:(ⅰ)tuning surface electrical properties,(ⅱ)modifying surface morphology,and(ⅲ)oxidating ***,regulating electrical contacts and handling with radiation damage and ion implantation have also been discussed in device *** each category,universal annealing conditions were speculated to figure out the corresponding problems,and some unsolved questions were proposed *** review could construct a systematic thermal treatment strategy for various purposes and applications of β-Ga_(2)O_(3).

关键词： β-gallium oxide thermal treatment substrates devices

A simple route for preparation of TRIP-assisted Si-Mn steel with excellent performance using direct strip casting

在线全文

学校读者我要写书评

暂无评论

International Journal of Minerals,Metallurgy and Materials 2024年第10期31卷 2173-2181页

作者： hui Xu Lejun Zhou Wanlin Wang yang Yi School of Metallurgy and Environment Central South UniversityChangsha 410083China National Center for International Research of Clean Metallurgy Central South UniversityChangsha 410083China

The complex producing procedures and high energy-consuming limit the large-scale production and application of advanced high-strength steels(AHSSs).In this study,the direct strip casting(DSC)technology with unique sub-rapid solidification characteristics and cost advantages was applied to the production of low-alloy Si-Mn steel with the help of quenching&partitioning(Q&P)concept to address these *** this method with the conventional compact strip production(CSP)process,the initial microstructure formed under different solidification conditions and the influence of heat treatment processes on the final mechanical properties were *** results show that the initial structure of the DSC sample is a dual-phase structure composed of fine lath martensite and bainite,while the initial structure of the CSP sample consists of pearlite and *** volume fraction and carbon content of retained austenite(RA)in DSC samples are usually higher than those in CSP samples after the same Q&P *** samples typically demonstrate better comprehensive mechanical properties than the CSP *** DSC sample partitioned at 300℃ for 300 s(DSC-Pt300)achieves the best comprehensive mechanical properties,with yield strength(YS)of 1282 MPa,ultimate tensile strength(UTS)of 1501 MPa,total elongation(TE)of 21.5%,and product of strength and elongation(PSE)as high as 32.3 GPa·%.These results indicate that the excellent mechanical properties in low-alloy Si-Mn steel can be obtained through a simple process(DSC-Q&P),which also demonstrates the superiority of DSC technology in manufacturing AHSSs.

关键词： direct strip casting sub-rapid solidification quenching and partitioning TRIP-assisted AHSSs microstructure

Application of three-dimensional electron diffraction in structure determination of zeolites

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Structural Chemistry 2024年第4期43卷 39-47页

作者： Yuhang Li yang ling Yanhang Ma School of Physical Science and Technology&Shanghai Key Laboratory of High-resolution Electron Microscopy ShanghaiTech UniversityShanghai201210China

Zeolites have received great attention due to their wide applications in various fields such as catalysis,adsorp-tion/separation,ion exchange,*** the atomic crystal structure of zeolites is crucial to understanding their functions and exploring their *** to the difficulty of synthesizing large single crystals,the structures of many zeolites cannot be solved using conventional single-crystal X-ray diffraction(SCXRD)***-dimensional electron diffraction(3D ED)has witnessed rapid development during the past decade and has shown its powerful ability in the structure determination of *** this review,we will briefly introduce the history of 3D ED and summarize recent advances in the application of 3D ED for the analysis of zeolite structures,along with several typical examples in this research field.

关键词： Electron diffraction Three-dimensional electron diffraction Zeolite Structure solution Electron crystallography

Observation of ballistic-diffusive thermal transport in GaN transistors using thermoreflectance thermal imaging

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Rare Metals 2024年第1期43卷 389-394页

作者： Zhi-Ke Liu yang Shen Han-ling Li Bing-yang Cao Key Laboratory for Thermal Science and Power Engineering of Ministry of Education Department of Engineering MechanicsTsinghua UniversityBeijing 100084China

To develop effective thermal management strategies for gallium-nitride (GaN) transistors, it is essential to accurately predict the device junction temperature. Since the width of the heat generation in the devices is comparable to phonon mean free paths (MFPs) of GaN, phonon ballistic transport exists and can significantly affect the heat transport process.

关键词： temperature. transistors GaN