Fabrication and Characterization of Willemite Scaffolds Using Corn Stalk as a Novel Bio Template for Bone Tissue Engineering Applications

引用

Journal of Bionic Engineering 2023年第1期20卷 16-29页

作者： Zahra Yahay Seyed Mehdi Mirhadi fariborz tavangarian Department of Cellular Biotechnology Cell Science Research CenterRoyan Institute for BiotechnologyACECRIsfahan81593-58686Iran Department of Materials Engineering Shahreza BranchIslamic Azad UniversityShahrezaIsfahan86145-311Iran Mechanical Engineering Program School of ScienceEngineering and TechnologyPennsylvania State UniversityHarrisburgMiddletownPA17057USA

In this paper,we used Corn Stalk(CS)as a renewable and economical bio template to fabricate willemite scaffolds with the potential application in skull bone *** was used as a sacrificial template to synthesize the *** scaffolds with the chemical formula of Zn2SiO4 and pore size in the range of 3 to 10µm could be successfully synthesized by soaking CS in the willemite solution for 24 h and sintering at 950°C for 5 *** porosity of the samples was controlled by the soaking time(between 12 and 48 h)in the willemite solution from 5 to 35%,*** properties of these scaffolds showed a good approximation with cranial bone *** addition,cytotoxicity assays(MTT)were performed on Human Bone Marrow Stromal cells(HBMSc)and A172 human glioblastoma cell lines by direct and indirect culture methods to estimate their toxicity for bone and nerve cells,*** Phosphatase(ALP)activity and DAPI/Phalloidin cell staining were also performed to investigate the efficiency of the scaffolds for bone tissue engineering *** results showed that the scaffolds had good biocompatibility with both HBMSC and A172 cells,noticeable improvement on ALP activity,and great apatite formation ability in Simulated Body Fluid(SBF).All the evidence ascertained that willemite scaffolds made by corn stalks could be a useful candidate for bone tissue engineering applications.

关键词： Corn stalk Bio template Bioactive ceramics-Scaffolds Bone tissue engineering

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Structural characterization and strengthening mechanism of forsterite nanostructured scaffolds synthesized by multistep sintering method

引用

Journal of Materials Science & Technology 2018年第12期34卷 2263-2270页

作者： fariborz tavangarian Abbas Fahami Guoqiang Li Mohammadhassan Kazemi Anoosha Forghani Mechanical Engineering Program School of ScienceEngineering and TechnologyPennsylvania State University Department of Mechanical Engineering Texas A&M University Department of Mechanical and industrial Engineering Louisiana State University Department of Mechanical and Aerospace Engineering University at Buffalo Department of Biomedical Engineering Millennium Science ComplexPennsylvania State UniversityUniversity Park

In this study, highly porous forsterite scaffolds with interconnected porosities were synthesized using multi-step sintering(MSS) method. The starting powder was nanosized forsterite, which was synthesized from talc and magnesium carbonate powders. The phase composition, average particle size and morphology of the produced forsterite powder were characterized by X-ray diffraction technique(XRD) and transition electron microscopy(TEM). Forsterite scaffolds were produced by foamy method using polymeric sponges. MSS process including three steps was used to efficiently sinter the forsterite nanopowders without destroying the initial porous structure of polymeric sponges. The results showed that MSS technique is an efficient and appropriate procedure to produce highly porous forsterite scaffolds with pore size in the range of 100-300 μm. The compressive strength, compressive modulus and porosity of C12 specimen(sintered at 1650℃ for 1 h with subsequent annealing at 1000℃ for 1000 min) was 1.88 MPa, 29.2 MPa, and 72.4%, respectively, which is very close to that of cancellous bone. The approach studied in this research can be developed for other nanostructure ceramics to produce highly porous scaffolds with interconnected porosities for load bearing applications.

关键词： Forsterite Multi-step sintering Scaffolds Porosity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：