Comparative study on CO_2.corrosion behavior of N80,P110,X52.and 13Cr pipe lines in simulated stratum water

Science China(Technological Sciences) 2010年第9期53卷 2342-2349页

作者： cai yidong1,guo pengchao1,{2.,chen shiyu2.& liu junlai3 1 school of energy resources,China university of geosciences,beijing 100083.China 2.school of Materials Science and Engineering,university of Science and Technology beijing,beijing 100083.China 3 school of Earth Sciences and resources,China university of geosciences,beijing 100083.China school of energy {2. China University of Geosciences

To better understand the carbon dioxide (CO2. corrosion behavior of carbon steel and its influence on petroleum development (including drilling,production and transportation) in the Daqing Oilfield,CO2.corrosion behaviors of N80,P110,X52.and 13Cr pipe lines in simulated solution at high temperature and high pressure condition are investigated by dynamic corrosion experiments,scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDS) *** show that the corrosion rate of all pipe lines increases quickly when CO2.partial pressure increases from 0.5 to 1.5 MPa,but it slows down when CO2.partial pressure further increases from 1.5 to 4.5 MPa,during which localized corrosion is *** the experimental temperature ranges from 60 to 12.°C,localized corrosion *** corrosion rate of all pipe lines decreases sharply when the temperature changes from 60 to 100°C,and it becomes stable after the temperature is higher than 100°*** the flow rate is in the range of 0–1.5 m/s,the corrosion rate of sample X52.remains unchanged,but localized corrosion gradually becomes very serious when the flow rate further *** analyzing the corrosion product scales of sample 13Cr,some remarkable phenomena are *** the temperature range of 60–100°C,the corrosion product scales are loose and thick,but become very compact when the temperature increases above 100°*** the later case,localized corrosion is *** main components of the corrosion product scales are FeCO3 and Cr2.3.

关键词： CO2 corrosion pipe lines weight loss SEM EDS

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：