Preparation and Properties of Macroporous Silicon Nitride Ceramics by Gelcasting and Carbonthermal Reaction

在线全文

学校读者我要写书评

暂无评论

Journal of materials science & Technology 2005年第6期21卷 894-898页

作者： Wen ZHANG, Hongjie WANG+ and Zhihao JIN state key {2. for mechanical behavior of materials, school of materials science and engineering, xi’an jiaotongUniversity, {12., china state key {2. for mechanical behavior of materials School of Materials Science and Engineering Xi'an Jiaotong University Xi'an 710049 China

Macroporous silicon nitride （Si3N4） ceramics with high strength, uniform structure and relatively high porosity were obtained by gelcasting and carbonthermal reaction in a two-step sintering technique. Microstructure and composition were investigated by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, X-ray diffraction （XRD）. Open porosity, pore size distribution and basic mechanical performance were measured by Archimedes method, mercury intrusion porosimetry and three-point bending methods, respectively. SEM and TEM results revealed that pores were formed by elongated β-Si3N4. SADP measurement proved the formation of SiC particles. The SiC granules were beneficial for the formation of high ratio elongated β-Si3N4, and at proper amount, they also acted as reinforcement phase. Thermodynamic analysis indicated that the mechanisms of the reactions were mainly associated with liquid-solid reaction and gas-liquid reaction.

关键词： Ceramics Silicon nitride Silicon carbide X-ray diffraction

Mechanism of Combustion Synthesis of TiC-Ti Cermet

在线全文

学校读者我要写书评

暂无评论

Journal of Wuhan University of Technology(materials science) 2007年第3期22卷 502-505页

作者：肖国庆 school of materials {2. and engineering Xi’an University of Architecture and Technology

In order to investigate the mechanism of combustion synthesis of TiC-Ti cermet, a mixture of Ti and C was used for a combustion front quenching test, and the microstructural evolution in the quenched sample was analyzed by scanning electron microscopy （SEM） and energy dispersive X-ray （EDX）. Also, a temperature-time profile of the combustion reaction was measured. Based on the experimental results, a reaction-dissolution-precipitation mechanism of the combustion synthesis of TiC-Ti was proposed.

关键词： TiC-Ti cermet combustion synthesis combustion front quenching method

Ultralight X-type lattice sandwich structure (Ⅱ):Micromechanics modeling and finite element analysis

在线全文

学校读者我要写书评

暂无评论

science china(Technological sciences) 2009年第9期52卷 2670-2680页

作者： ZHANG QianCheng1,CHEN AiPing 2.CHEN ChangQing2.3 & LU TianJian2.1 state key {2. for mechanical behavior of materials,school of material science and engineering,xi’an jiaotong University,xi’an 710049,china 2.MOE key {2. for Strength and Vibration,school of Aerospace,xi’an jiaotong University,xi’an 710049,china 3 Department of engineering Mechanics,AML,Tsinghua University,Beijing 100084,china state key {2. for mechanical behavior of materials School of Material Science and Engineering Xi’an Jiaotong University Xi’an China MOE key laboratory for Strength and Vibration School of Aerospace Xi’an Jiaotong University Xi’an China Department of engineering Mechanics AML Tsinghua University Beijing China

The methods of homogenization and finite elements are employed to predict the effective elastic constants and stress-strain responses of a new type of lattice structure,the X-structure proposed by the authors in a companion paper. It is shown that in most cases the predictions by the equivalent homogenization theory agree well with the experimental and 3-dimensional finite element calculated results. The theoretical and numerical study supports the argument that the X-structure is superior to the pyramid lattice structure in terms of mechanical strength.

关键词： sandwich panel lattice structure equivalent homogenization finite element model

Structure and electrochemical properties of low-cobalt La_(1-x)Li_xNi_(3.2.Co_(0.3)Al_(0.3) (0≤x≤0.2. hydrogen storage electrode alloys

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2006年第Z1期25卷 1-6页

作者： WEI Xuedong LIU Yongning ZHANG Peng state key {2. for mechanical behavior of materials School of Material Science and Engineering Xi''an Jiaotong University Xi''an 710049 China State Key Laboratory for Mechanical Behavior of Materials School of Material Science and Engineering Xi''an Jiaotong University Xi''an 710049 China State Key Laboratory for Mechanical Behavior of Materials School of Material Science and Engineering Xi''an Jiaotong University Xi''an 710049 China

The structure and electrochemical properties of a new low cobalt hydrogen storage electrode alloys La1-xLixNi3.2.o0.3Al0.3 (0≤x≤0.2. were investigated with a different additions of Li in replacement of La. With the increase of Li contents the maximum discharge capacity increases from 2.0 mAh·g-1(x=0) to 32..4 mAh·g-1(x=0.1) and the cycle stability is improved correspondingly. The capacity decay can remain 2..6% (x=0.2. after 2.0 charge/discharge cycles. The high rate discharge(HRD) ability of the alloys(x≤0.1) is improved and the best HRD is 34.1%(x=0.1) under the discharge current density 12.0 mA·g-1. It is found that the prepared alloys are basically composed of LaNi5 as matrix phase and LaNi3 as second phase(x≤0.1). But the abundance of LaNi3 phase dramatically decreases with increasing x. When x=0.2. a new phase Al(NiCo)3 is formed.

关键词： hydrogen storage alloy microstructure high rate discharge ability cycling stability

Quasi-nano wear mechanism under repeated impact contact loading

在线全文

学校读者我要写书评

暂无评论

science china(Technological sciences) 2010年第6期53卷 1583-1589页

作者： ZHU JinHua1,REN xiangHong1,2.ZHANG JianJun1,3,XU YunHua1,3 & LU Zhengxin1,4 1 {2. key laboratory for mechanical behavior of materials,xi’an jiaotong University,xi’an 710049,china 2.xi’an Research Institute of High-tech,xi’an 71002.,china 3 school of materials science and engineering,xi’an University of Architecture and Technology,xi’an 710055,china 4 school of materials science and engineering,xi’an University of Technology,xi’an 710049,china state key {2. for mechanical behavior of materials Xi’an Jiaotong University Xi’an China xi’an Research Institute of High-tech Xi’an China school of materials {2. and engineering Xi’an University of Architecture and Technology Xi’an China school of materials {2. and engineering Xi’an University of Technology Xi’an China

A new quasi-nano wear mechanism (QNWM) has been proposed in this paper based on the facts of wear curve turning under high energy impact contact *** characteristic is that the wear rate of QNWM is only 1/10-1/3 that of delamination mechanism at the same energy *** diameters of wear debris and pits on the worn surfaces fall into the quasi-nanometer scale (about 50-12. nm).The necessary and sufficient conditions,which bring about the QNWM,are:(i) the nano-structure (nano-crystalline + amorphous phase) in impact contact surface layer has formed by the intensive impact strain;(ii) the delamination wear cracking in sub-surface layer must be restrained;(iii) the microcracks of QNWM are produced in amorphous phase of surface nano-structure layer rather than in nano-crystalline.

关键词： impact wear quasi-nano wear mechanism delamination wear mechanism nano-structure

Microstructure and mechanical Properties of Nanocrystalline Tungsten Thin Films

在线全文

学校读者我要写书评

暂无评论

Journal of materials science & Technology 2010年第1期26卷 87-92页

作者： H.L. Sun, Z.X. Song, D.G. Guo, F. Ma and K.W. Xu state key {2. for mechanical behavior of materials, school of materials science and engineering, xi an jiaotong University, {12., china state key {2. for mechanical behavior of materials School of Materials Science and Engineering Xi'an Jiaotong University Xi'an 710049 China

Tungsten （W） thin films were prepared by magnetron sputtering onto Si （100） substrates. Their microstructures were characterized by X-ray diffraction （XRD）, field emission scanning electron microscopy （FE-SEM） and transmission electron microscopy （TEM）. The hardness and modulus were evaluated by nanoindentation. It is found that a 30 nm Cr sticking layer induces structure changes of deposited W film from β-W to α-W structure. In addition, remarkable hardness enhancement both for the deposited and annealed W films, were compared with that of bulk coarse-grained W, although their nanoindentation modulus is very close to that of corresponding bulk W. The intrinsic reasons that lead to structure changes and super hardness are discussed.

关键词： Tungsten film Microstructure Nanoindentation Hardness Modulus

Effect of Annealing Ambience on the Chemical Stability of Zr-Si-N Diffusion Barrier

在线全文

学校读者我要写书评

暂无评论

材料热处理学报 2004年第5B期25卷 1225-1228页

作者： SONGZhong-xiao WANGYuan XUKe-wei LIUChun-liang keyLabforPhysicalElectronicsandDevicesMinistryofEducation Xi＇anJiaotongUniversity710049Xi＇anChina state-key{2.formechanicalbehaviorofmaterials Xi＇anJiaotongUniversity710049Xi＇anChina

Zr-Si-N films were deposited by RF magnetron sputtering (MS) technique. A Cu film on the top of Zr-Si-N films was prepared by DC pulsed magnetron sputtering. The Cu/Zr-Si-N systems were annealed in vacuum and N2.H2.gas mixture at 800°C, respectively. The structure of the films were characterized by X-ray diffraction (XRD), Auger electron spectroscopy (AES) and four-point probe method. The sheet resistances of the Cu/Zr-Si-N/Si contact systems annealed in N2.H2.gas mixture were lower than those of the specimens annealed in vacuum at 800°C. The residual oxygen contamination from vacuum annealing ambience influences the sheet resistances of the Cu/Zr-Si-N/Si contact systems due to residual oxygen contamination and/or voids in Cu films. Though thermal stabilities of the Cu/Zr-Si-N/Si systems were maintained up to 800°C when annealed in vacuum and N2.H2.gas mixture, the changes of thermal stability of specimens were noticeable. The vacuum can accelerate the oxidation and decomposition of Zr-Si-N barrier. On the contrary, N2.H2.gas mixture prevent from the Zr-Si-N barrier oxidation and decomposition.

关键词：扩散势垒 Zr-Si-N 退火化学稳定性

Thermodynamic Analysis of the Formation of In-situ Reinforced Phases In Cast Al-4.5Cu Alloy

在线全文

学校读者我要写书评

暂无评论

Journal of Wuhan University of Technology(materials science) 2008年第3期23卷 342-345页

作者：梁艳峰 state key {2. for mechanical behavior of materials School of Materials EngineeringXi’an Jiaotong University school of materials&Chemical {2. Xi’an Technological UniversityXi'an 710032China

The thermodynamic analysis of the formation of in-situ reinforced phases in （TiB2.Al3Ti）/Al-4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by differential thermal analysis（DTA）.The results show that although TiB2.possesses the strongest formation ability in Al-Ti-B ternary system, [Ti] is relatively excessive in the in-situ reaction and it combines with Al to form AlaTi phase. The reinforced phases are TiB2.and AlaTi in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ℃ and 1 032.℃.

关键词： in-situ composites thermodynamic, TiB2 Al3Ti

Melt-spun Al_(70-X)Si_(30)Mn_X (X=0,3,5,7,10) anode in lithium-ion batteries

在线全文

学校读者我要写书评

暂无评论

science china(Technological sciences) 2009年第8期52卷 2288-2294页

作者： SUN ZhanBo1, LI XuePeng1, WANG xiaoDong1, HU Qing1, ZHAO MingShu1, ZHU YaoMin2. LI Yan2.& SONG xiaoPing1 1 {2. of science, state key laboratory for mechanical behavior of materials, xi’an jiaotong University, {12., china 2.{2. of materials science and engineering, Henan University of science and Technology, Luoyang 471003, china school of science State Key Laboratory for Mechanical Behavior of Materials Xi’an Jiaotong University Xi’an China school of materials {2. and engineering Henan University of Science and Technology Luoyang China

Al70-XSi30MnX (X=0, 3, 5, 7, 10, mol%) ribbons were prepared by melt spinning. A supersaturated solid solution of Si and Mn in fcc Al and some microstructures consisting of nano grains were obtained. Some alloys with nano-sized grains exhibited high discharge capacities and favorable cycle properties. The capacity of more than 400 mAh/g could be obtained in melt-spun Al67Si30Mn3 alloy after 2. cycles and more than 300 mAh/g after 40 cycles. Li/Si and Li/Al compounds in the anodes of pure Al and pure Si were not detected in Al-Si-Mn alloys inserted by Li. It is considered that the formation of the supersaturated solid solution and refinement of microstructures have prevented the alloys from the forming the compounds with superfluous Li. As a result, the electrochemical properties have been improved.

关键词： Al-Si-Mn alloy melt spinning microstructure electrochemical property