Interface fracture characteristic and crack propagation investigations of thermal barrier coatings under tensile tests at elevated temperature
会议名称:《The Eighth International Conference on Fundamentals of Fracture(ICFF VIII)》
会议日期:2008年
学科分类:08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学]
关 键 词:thermal barrier coatings tensile test interface fracture toughness crack propagation
摘 要:Thermal barrier coatings(TBCs) have been extensively used in aircraft engines for improved durability and performance for more than fifteen *** this paper,thermal barrier coating system with plasma sprayed zirconia bonded by a MCrAlY layer to SUS304 stainless steel substrate were performed under tensile tests at 1000℃.The crack nucleation,propagation behavior of the ceramic coatings in as received and oxidized conditions were observed by high- performance camera and discussed in *** relationship of the traverse crack numbers in the ceramic coating and tensile displacement were recorded and used to describe the crack propagation mechanism of thermal barrier *** was found that the fracture/spallation locations of air plasma sprayed thermal barrier coating system mainly lay within the ceramic coating close to the bond coat interface by scanning electron microscope(SEM) and energy dispersive X-Ray(EDX). The energy release rate and interface fracture toughness of plasma-sprayed thermal barrier ceramic coatings were evaluated by the aid of Suo-Hutchinson *** calculations revealed that the energy release rate and fracture toughness ranged,respectively,from 22.15J·m to 37.8J·m and from 0.9MPa·m to 1.5MPa·*** results agree well with other experimental results.