FEM analysis for hot rolling process of AM60 alloy

作     者：丁汉材 KANAMORI Nao HONMA Tomoyuki KAMADO Shigeharu KOJIMA Yo 

作者机构：Department of Mechanical Engineering Nagaoka University of Technology 1603-1 Kamitomioka Nagaoka Niigata 940-2188 Japan 

出 版 物：《中国有色金属学会会刊：英文版》 (Transactions of Nonferrous Metals Society of China)

年 卷 期：2008年第18卷第A1期

页      面：242-246页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：AM60镁合金 流动性 有限元分析 FEM 

摘      要：The rolling of AM60 sheets for 50%reduction was analyzed with DEFORM to investigate the hot deformation process. The simulated results show that the sheet velocities at the entrance(21 mm/s) and at the exit(37 mm/s) are less and larger than roll velocity,*** the entrance to the neutral point,the velocity at the sheet surface is greater than that at the middle point of sheet in thickness,while that from the neutral point to the exit shows the opposite *** effective strain of the sheet increases from the entrance to the exit due to the continuous reduction in *** addition,the effective strain at the sheet surface reaches to 1.0 and is larger than that of 0.8 at the middle point of *** difference of effective strain in thickness direction has a much stronger effect on the recrystallized fraction than on the recrystallized grain *** minimum temperature of 347℃is obtained at the surface contacting directly with roll and the maximum temperature 388℃at the middle point of sheet in thickness.