Utilization of Thermally Treated Flue Gas Desulfurization (FGD) Gypsum and Class-C Fly Ash (CFA) to Prepare CFA-Based Geopolymer

作     者：郭晓潞 施惠生 Warren A Dick 

作者机构：Key Laboratory of Advanced Civil Engineering Materials (Tongji University) Ministry of Education School of Environment and Natural Resources the Ohio State University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2013年第28卷第1期

页      面：132-138页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National Natural Science Foundation of China(Nos.51208370,51172164) the Specialized Research Fund for the Doctoral Program of Higher Education(Nos.20110072120046,20090072110010)of China 

主　　题：flue gas desulphurization (FGD)gypsum class-C fly ash(CFA) geopolymer thermal treatment 

摘      要：The feasibility of utilization of flue gas desulfurization （FGD） gypsum and Class-C fly ash （CFA） to prepare CFA-based geopolymer were studied. The results showed that geopolymer made from 90% CFA and 10% FGD gypsum （FGDG） which was thermally treated at 800 ℃ for 1 h obtained the better compressive strength of 37.0 MPa. The micro characteristics and structures of the geopolymer samples of CFA and CFA-FGDG were tested by XRD, FT-IR, and SEM-EDXA after these samples cured at 75 ℃ for 8 h followed by 23 ℃ for 28 d. Both the geopolymer samples of CFA and CFA-FGDG have significant asymmetric stretching of A1-O/Si-O bonds and Si-O-Si / Si-O-A1 bending band. In geopolymer sample of CFA-FGDG, a small quantity of lathy products probably being the ettringite wrapped over the spherical fly ash particle, and the concentration of sulfur is much more than that in geopolymer sample of CFA. It is indicated that FGD gypsum may react during alkali-activated and geopolymeric process.