Microstructure and properties of novel Al-Ce-Sc,Al-Ce-Y,Al-Ce-Zr and Al-Ce-Sc-Y alloy conductors processed by die casting,hot extrusion and cold drawing

作     者：Weiyi Wang Qinglin Pan Geng Lin Xiaoping Wang Yuqiao Sun Xiangdong Wang Ji Ye Yuanwei Sun Yi Yu Fuqing Jiang Jun Li Yaru Liu Weiyi Wang;Qinglin Pan;Geng Lin;Xiaoping Wang;Yuqiao Sun;Xiangdong Wang;Ji Ye;Yuanwei Sun;Yi Yu;Fuqing Jiang;Jun Li;Yaru Liu

作者机构：School of Materials Science and EngineeringCentral South UniversityChangsha 410083China Light Alloy Research InstituteCentral South UniversityChangsha 410083China Hunan Oriental Scandium Industry Co.Ltd.Changsha 410100China Manufacturing CenterCRRC Times Electric Co.Ltd.Zhuzhou 412001China Institute of Metal ResearchChinese Academy of SciencesShenyang 110016China The Second Xiangya HospitalCentral South UniversityChangsha 410011China 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：2020年第58卷第23期

页      面：155-170页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：supported financially by the Key Research and Development Program of Guangdong Province(NO.2020B010186002) the Science and Technology Major Project of Hunan Province(NO.2017GK4002) 

主　　题：Al-Ce-Sc-Y alloy Electrical conductivity Mechanical properties Second phase Nano-size precipitates 

摘      要：In order to overcome the trade-off between the strength and electrical conductivity of aluminum alloy conductors,the new Al-Ce-Sc,Al-Ce-Y,Al-Ce-Zr and Al-Ce-Sc-Y alloys were prepared by die casting,high temperature homogenization treatment,hot extrusion and cold *** Sc and Y eliminated the dendrite segregation of the as-cast Al-0.2 Ce alloy and promoted the formation of equiaxed grains with the average grain size of 142.5μ*** Al-0.2 Ce-0.2 Sc-0.1 Y alloy inherited the great tensile properties of Al-0.2 Ce-0.2 Sc alloy and the high electrical conductivity of Al-0.2 Ce-0.1 Y alloy *** cold drawing and annealing at 200℃for 5 h,the ultimate tensile strength of Al-0.2 Ce-0.2 Sc-0.1 Y alloy reached 200 MPa and 198 MPa,the elongation reached 6.8%and 8.5%,and the electrical conductivity reached 61.01%and 61.77%,*** main second phase of Al-0.2 Ce-0.2 Sc-0.1 Y alloy after hot extrusion were Al_(13)Fe_3 Ce containing a few Y and Si *** larger size and proportion of the second phase greatly reduced the concentration of solute Fe and Si atoms and the addition of Y significantly decreased the density of defects after cold drawing compared to Al-0.2 Ce-0.2 Sc alloy,which improved electrical conductivity of the ***,the dispersed and coherent nano-size Al_3 Sc precipitions of Al-0.2 Ce-0.2 Sc-0.1 Y alloy greatly improved strength,elongation and heat *** with Al-0.2 Ce-0.2 Sc alloy,the lower density of dislocation,stacking fault and subgrain boundary and the larger size of Al_3 Sc precipitions with enrichment of Y atoms enable the Al-0.2 Ce-0.2 Sc-0.1 Y alloy to maintain high strength,elongation and electrical conductivity after annealing.