Effects of GH Admixture on the Early Strength of Fly Ash Concrete and Mortar

作     者：亢景付 KANG Jingfu, WANG Xiufen* (School of Civil Engineering, Tianjin University, Tianjin 300072, China)

作者机构：School of Civil Engineering Tianjin University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2008年第23卷第5期

页      面：755-760页

核心收录：

学科分类：08[工学] 081304[工学-建筑技术科学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0813[工学-建筑学] 0702[理学-物理学] 

基　　金：the National Nature Science Foundation of China (No. 50679054) 

主　　题：building materials fly ash concrete GH admixture strength microstructure 

摘      要：The enhancement effects of GH admixture on the early strengths of fly ash concrete and mortar were studied, and the mechanism was analyzed by X-ray diffraction （XRD） and scanning electro microscope （SEM）. Experimental results show that, by the incorporation of GH admixture, both of cement hydration and pozzolanic reaction of fly ash are accelerated, the strengths of fly ash concrete and mortar are enhanced noticeably, especially the early strength. With a mixture design of 200 kg/m^3 OPC （Ordinary Portland Cement ）, 200 kg/m^3 fly ash and 50 kg/m^3 GH admixture, the strength of concrete at 1 d, 3 d and 28 d reaches 25 MPa, 50 MPa and 70 MPa respectively.