Fractal Dimensions of Hydrogen Induced Brittle Fracture of Titanium Aluminide

作     者：Yue ZHANG Yanbin WANG Lijie QIAO Wuyang CHU Chimei HSIAO Dept.of Materials Physics,University of Science and Technology,Beijing,Beijing,100083,China 

出 版 物：《Journal of Materials Science & Technology》 (材料科学技术（英文版）)

年 卷 期：1993年第9卷第5期

页      面：338-342页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：titanium aluminide hydrogen induced cracking tractal dimension 

摘      要：The relationship between the stress intensity factor K_1~* required for brittle crack initiation and propa- gation and the fractal dimension D_F of the fracture surface was derived,i.e, InK_1~*=(1/2)In2γE +(1/2)In(d_f/L_0)(1-D_F) The real surface energy can be calculated based on the measured linear relation of the InK_1~* vs D_F, The equation is not only suitable for the overload fracture but also for the delayed fracture,e.g. hydrogen induced cracking (HIC) and stress corrosion cracking (SCC).The experiment results showed that the hydrogen induced delayed cracking occurred in the Ti-24AI-11 Nb alloy during dy- namic charging,and the threshold stress intensity factor was very low,i.e..K_(IH)/K_(IC)= *** ex- perimental relationship between the stress intensity factor K_1~* and D_F was consistent with the theo- retical equation.