The Influence of Atmospheric Pressure on Air Content and Pore Structure of Air-entrained Concrete

作     者：LI Yang WANG Zhendi WANG Ling 李扬;WANG Zhendi;王玲

作者机构：State Key Laboratory of Green Building MaterialsChina Building Materials AcademyBeijing 100024China 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2019年第34卷第6期

页      面：1365-1370页

核心收录：

学科分类：08[工学] 081304[工学-建筑技术科学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0813[工学-建筑学] 

基　　金：Funed by the National Key R&D Program of China(No.2017YFB0309903) 

主　　题：low atmospheric pressure air-entrained concrete air content pore structure surface tension 

摘      要：To study the effect of atmospheric pressure on the properties of fresh and hardened airentrained concrete, three kinds of air entraining agents were used for preparing air-entrained concrete in the plateaus(Lhasa, 61 kPa) and the plains(Beijing, 101 kPa). Air content, slump, compressive strength and pore structure of the three air-entrained concretes were tested in these two places. It is found that the air content of concrete under low atmospheric pressure(LAP) is 4%-36% lower than that of concrete under normal atmospheric pressure(NAP), which explaines the decrease of slump for air-entrained concrete under LAP. Pore number of hardened concrete under LAP is reduced by 48%-69%. While, the proportion of big pores(pore diameter 1 200 μm) and air void spacing factor are increased by 1.5%-7.3% and 51%-92%, respectively. The deterioration of pore structure results in a 3%-9% reduction in the compressive strength of concrete. From the results we have obtained, it can be concluded that the increase of critical nucleation energy of air bubbles and the decrease of volumetric compressibility coefficient of air in the concrete are responsible for the variation of air content and pore structure of concrete under LAP.