Mechanical Alloying Effect on the Structure of Fe-Al-(Si) Alloy
Mechanical Alloying Effect on the Structure of Fe-Al-(Si) Alloy作者机构:SOUTHEAST UNIVDEPT MECH ENGNNANJING 210096PEOPLES R CHINA NANJING UNIVDEPT CHEMNANJING 210008PEOPLES R CHINA NANJING UNIVDEPT PHYSNANJING 210008PEOPLES R CHINA
出 版 物:《Journal of Materials Science & Technology》 (材料科学技术(英文版))
年 卷 期:1997年第13卷第3期
页 面:219-222页
核心收录:
学科分类:0817[工学-化学工程与技术] 0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
摘 要:The mechanical alloying effects on the structures of Fe71.3Al28.4(CeO2)(0.3) and Fe73.3Al9.8-Si-16.6(CeO2)(0.3) samples have been investigated mainly by Mossbauer spectroscopy and X-ray diffraction. it is found that with the increase of milling time, a substituting disordered alpha-Fe solution is formed gradually and almost completed after milled for 72 h. Further increasing milling time causes the atomic rearrangement within the powders. Correspondingly, the average lattice parameter and average crystalline size change until 72 h and remain constant after 72 h. The addition of Si leads to the higher disordered degree reflected in the smaller average hyperfine field and larger mean square deviation.