Nonlinear Optical Properties in Bismuth-based Glasses

作     者：章健良 ZHANG Jianliang1, 2, NIE Qiuhua1, DAI Shixun1, XU Tiefeng1, CHEN Feifei1, SHEN Xiang1, WANG Xunsi1 (1. Faculty of Information Science and Engineering, The State Key Laboratory Base of Novel Functional Materials and Preparation Science, Ningbo University, Ningbo 315211, China;2. People’s Liberation Army with Number of 91428)

作者机构：Faculty of Information Science and Engineering The State Key Laboratory Base of Novel Functional Materials and Preparation Science Ningbo University People's Liberation Army with Number of 91428 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2011年第26卷第1期

页      面：61-64页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National Natural Science Foundation of China (No.60677015) the Science and Technology Department of Zhejiang Province (No.2007C21122) the Natural Science Foundation of Ningbo (No.2006A610020) 

主　　题：bismuth glasses optical band gap third-order nonlinear Z-scan 

摘      要：A series of glasses with high Bi2O3 content of Bi2O3-B2O3-WO3 ternary system were chosen and prepared .Their densities and linear refractive indices increase with increasing WO3 content. The optical band gaps Eopt of glasses obtained from ultraviolet absorption edges decreases with increase of WO3 content. Z-scan technique was carried out to investigate the third-order nonlinear optical properties of the glasses. It is found that the nonlinear refraction γ increases with decreasing the optical band gap Eopt, since an increase of WO3 content can promote the non-bridging oxygen ion content, and the highest γ value of samples is 1.173×10-14 cm2/W. The results show that these glasses are potential materials in the application of third-order nonlinear optics field.