Precipitation and Solid Solution of Titanium Carbonitride Inclusions in Hypereutectoid Tire Cord Steel
Precipitation and Solid Solution of Titanium Carbonitride Inclusions in Hypereutectoid Tire Cord Steel作者机构：The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and Technology
出 版 物：《Journal of Iron and Steel Research International》 (J. Iron Steel Res. Int.)
年 卷 期：2016年第23卷第4期
页 面：338-343页
核心收录：
学科分类：080503[工学-材料加工工程] 08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化]
主 题：hypereutectoid tire cord steel titanium carbonitride inclusion precipitation solidification solid solution billet heating
摘 要：The properties of titanium carbonitride Ti（CxN1-x） inclusions precipitated during solidification of tire cord steels and the thermodynamic conditions for their decomposition and solid solution during billet heating were investigated using a thermodynamics method. The solid solution of Ti（CxN1-x） inclusions during high-temperature heating was also studied experimentally. The results revealed that： （1） the higher the content of carbon in the tire cord steel is, the greater the value of .r in the Ti（CxN1-x） inclusions is; （2） the higher the content of carbon in the tire cord steel is, the earlier the Ti（CxN1-x） inclusions precipitated during the solidification process and the lower the solidification front temperature is during precipitation; （3） when an 82A steel sample was heated to 1087℃, the Ti（CxN1-x） inclusions possess the thermodynamic conditions of decomposition and solid solution; and （4） when 82A samples were heated to 1150 and 1 250℃, the total number of Ti（CxN1-x） inclusions larger than 5μm in diameter decreased by 55.0% and 70.3%, respectively. In addition, although smaller inclusions with diameter less than 2 μm continued to decompose when the sample was heated at 1 250℃ for 2 h and then cooled to 1000℃ in the furnace, the number of inclusions larger than 5 μm in diameter increased.