Tribological Properties of a Dendrite-reinforced Ti-based Metallic Glass Matrix Composite under Different Conditions
Tribological Properties of a Dendrite-reinforced Ti-based Metallic Glass Matrix Composite under Different Conditions作者机构:Research Institute of Surface EngineeringTaiyuan University of Technology
出 版 物:《Journal of Iron and Steel Research International》 (Journal of Iron and Steel Research, International)
年 卷 期:2016年第23卷第1期
页 面:57-63页
核心收录:
学科分类:0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0703[理学-化学] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
基 金:Item Sponsored by National Natural Science Foundation of China(51371122,51401141) Program for the Innovative Talents of Higher Learning Institutions of Shanxi Province of China(2013) Youth Science Foundation of Shanxi Province of China(2014021017-3)
主 题:sliding wear surface topography electrochemical test pitting corrosion
摘 要:The tribological properties of the in-situ dendrite-reinforced metallic glass matrix composite(Ti42Zr22V14-Cu5Be17)prepared by copper mould casting were analyzed at different normal loads under the dry condition and *** results showed that the average value of the frictional coefficients and micro-hardness ascended with increasing the normal load,while the wear rate showed a trend of decline under the dry *** electrochemical test results showed that the surface of samples was pitting corroded in the *** matrices were corroded *** the dendrites were exposed,leading to the damage of the *** the frictional coefficients and wear rate of the composite in the rainwater were larger than those under the dry condition,primarily owing to the corrosion of chloride ions on the worn *** wear mechanisms of composites were mainly adhesive wear,accompanied by the abrasive wear under the dry condition and corrosive wear in the *** composites have higher wear resistance both under the dry condition and rainwater due to the lower wear rate.