Effect of Homogenizing Procedures on the Properties of Reaction Sialon Suspension

作     者：Xavier Venceslau Kexin Chen José M F Ferreira 

作者机构：Department of Ceramics and Glass EngineeringCICECO University of AveiroDepartment of Ceramics and Glass EngineeringCICECO University of AveiroDepartment of Ceramics and Glass EngineeringCICECO University of Aveiro PortugalPortugalPortugal 

出 版 物：《厦门大学学报（自然科学版）》 (Journal of Xiamen University：Natural Science)

年 卷 期：2002年第41卷第S1期

页      面：132-133页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：Effect of Homogenizing Procedures on the Properties of Reaction Sialon Suspension 

摘      要：Homogeneous, high concentrated ceramic suspensions wi th low viscosity are the key controlling factors for the production of ceramic c omponents through colloidal processing. A well-dispersed suspension can be obta ined by choosing suitable dispersant, solvent, particle size distribution etc. B esides these factors, the homogenizing procedure is also a key step. In this paper, reaction sialon suspensions were prepared using 3-wt% KD1 as dis persant in organic media composed of 60-vol% methyletheylketone and 40-vol% et hanol. Different homogenizing procedures have been used and compared, including planetary milling, low energy ball milling and ultrasonic disaggregation. The ef fects of different homogenizing routes and mixing times on the rheology and stab ility of suspensions, and on the microstructure of slip casting green bodies, ha ve been studied. The varying dispersion efficiencies observed could be attribute d to differences in deagglomeration degrees achieved and in adsorption amount of dispersant onto the surface of reaction sialon powders.