Phase composition of SiC-ZrO2 composite materials synthesized from zircon doped La2O3
Phase composition of SiC-ZrO2 composite materials synthesized from zircon doped La2O3作者机构:School of Materials and Metallurgy Northeastern University Shenyang 110004 China School of Materials and Metallurgy Northeastern University Shenyang 110004 China
出 版 物:《Journal of Rare Earths》 (稀土学报(英文版))
年 卷 期:2009年第27卷第5期
页 面:806-810页
核心收录:
学科分类:080603[工学-有色金属冶金] 0709[理学-地质学] 0819[工学-矿业工程] 08[工学] 0806[工学-冶金工程] 0708[理学-地球物理学] 0703[理学-化学]
基 金:Project supported by the National Natural Science Foundation of China (50274021) and Baoshan Iron and Steel Co. Ltd
主 题:composite materials carbothermal reduction zircon lanthanum oxide rare earths
摘 要:A study was carried out to determine the optimum parameters for synthesis of SiC-ZrO2 composite materials by carbothermal re-duction of zircon. Test samples were prepared by mixing average mesh size of less than 30 μm of carbon black and 40 μm of zircon with C/ZrSiO4 mass ratio of 0.2 and the extra addition amount of La2O3 was 0, 1 wt.% and 2 wt.%. Prepared samples were subjected to the car-bothermal reduction process at temperatures of 1723, 1753, 1773 and 1803 K for 4 h, respectively. The carbothermal reduction process was conducted in an atmosphere controlled tube furnace at an argon flow of 1.5 L/min. All products were examined by X-ray diffraction (XRD) to determine the transformation. The results showed that the best transformation of SiC-ZrO2 composite materials occurred at 1803 K for 4 h with the amount of 2 wt.%La2O3.