The Oxidation State of Sulfur Detected in Na_2O-CaO-SiO_2 Float Glass by X-ray Absorption Near Edge Structure Spectra

作     者：孟政 JIANG Hong HUANG Yourong LI Changjiu WANG Jinzhen CUI Zhu 

作者机构：China Building Materials Academy College of Materials and Chemical Engineering Hainan University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2013年第28卷第1期

页      面：79-81页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National Natural Science Foundation of China(No.50972136) 

主　　题：XANES sulfur K-edge Na20-CaO-SiO2 float glass oxidation state sulfur speciation 

摘      要：The oxidation state of sulfur is detected in Na20-CaO-SiO2 float glass by synchrotron radiation X-ray absorption near edge structure （XANES） spectra at the sulfur K edge. The measured spectra show the only presence of S^6＋ in the Na20-CaO-SiO2 float glass and the oxidation state of sulfur do not change with the increase of glass depth. It is also found that, after the melt has gone through the molten tin bath, the S^6＋ is the dominant species, but S^2- is also present on both surfaces. It is not certain whether cation bonds to S^2- or not, because there are many cations dissolved in the melted tin which makes the spectrum complicated.