Plasma Niobium Surface Alloying of Pure Titanium and its Oxidation at 900 ℃

作     者：WANG Wen-bo ZHONG Xu HE Zhi-yong WANG Zhen-xia ZHANG Ping-ze 

作者机构：Research Institute of Surface Engineering Taiyuan University of Technology Taiyuan 030024 China Nanjing University of Aeronautics and Astronautics Nanjing 210016 China 

出 版 物：《Chinese Journal of Aeronautics》 (中国航空学报（英文版）)

年 卷 期：2007年第20卷第2期

页      面：111-114页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

主　　题：niobium pure titanium plasma surface alloying oxidation 

摘      要：A niobium-modified layer on pure titanium surface was obtained by means of double glow plasma surface alloying technique. The modified layer was uniform, continuous, compact and well adhered to the substrate. The niobium composition in the modified layer decreased gradually from the surface to the substrate. The oxidation behavior of the niobium-modified layer was investigated and com- pared with the untreated surface at 900 ~C for 100 h. Characterization of the layers was performed using X-ray diffraction and scanning electron microscope, respectively. The test results show that the oxidation behavior of pure titanium was improved by niobium alloying process. Niobium has a positive influence on the oxidation resistance.