Stress Oriented Hydrogen Induced Cracking of Linepipe Steel
Stress Oriented Hydrogen Induced Cracking of Linepipe Steel作者机构:Pohang University of Science and Technology Graduate Institute of Ferrous TechnologySan 31Hyoja-DongPohang 790-784Korea
出 版 物:《Journal of Iron and Steel Research International》 (钢铁研究学报(英文版))
年 卷 期:2011年第18卷第S1期
页 面:121-128页
核心收录:
学科分类:0806[工学-冶金工程] 08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程(可授工学、理学学位)]
主 题:linepipe steel stress oriented hydrogen induced cracking hydrogen induced cracking metallurgical factor diffusible hydrogen
摘 要:The stress oriented hydrogen induced cracking (SOHIC) is a typical hydrogen embrittlement phenomenon occurring in the linepipe steels exposed to sour environment containing H 2 S ***,even recently,the cracking mechanism of SOHIC has not been clarified because of lacking in the empirical data on the actual failure mode of SOHIC *** factors affecting SOHIC are discussed in terms of metallurgy of high strength linepipe steel and hydrogen *** cracking mechanisms of SOHIC are examined by comparing them with the empirical failure mode of SOHIC which is developed by observation of the actual fracture sites of the hydrogen induced blister cracking (HIBC) and secondary ***,the correlation between SOHIC and HIC is discussed.