Cycling Hardening and Serration Yielding of Fe-Ni-Cr Alloy at High Temperature under Out-phase TMF

作     者：何庆复 HE Qingfu (Department of Mechanical Engineering, Beijing Jiaotong University, Beijing 100044, China)

作者机构：Department of Mechanical EngineeringBeijing Jiaotong University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2009年第24卷第3期

页      面：428-431页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0702[理学-物理学] 

主　　题：hysteresis loop cycling hardening serration yield out-phase isothermal cycling 

摘      要：Behaviour of hardening and serration yield of a Fe-Ni-Cr alloy under isothermal cycling （ISC） and out-phase TMF was studied on the basis of varied hysteresis loops. Cycling hardening and serrated yielding for ISC depend on the temperature and the total strain range, stronger hardening with serrated yielding at higher strain range under ISC at 600 ℃, but no hardening and serrated yielding occurred under ISC at 800 ℃. Stronger hardening with stress serration occurred at the thermal path going to the lowest temperature, no stress serration occurred at the highest temperature under the out-phase. The hardening also depends on the total strain range, higher total strain range with lower cycling temperature resulted in a stronger hardening and remarkable serration yielding behavior. Weaker hardening without serrated yielding occurred at near 800℃ may due to an obvious cycling stress drop under out-phase TMF. Change in the shape of the hysteresis loops also expresses the degree of the damage of the tested alloy under out-phase and ISC.