Durability of Alite-calcium Barium Sulphoaluminate Cement

作     者：芦令超 LU Lingchao,LU Zeye,LIU Shiquan,WANG Shoude,CHENG Xin (School of Materials Science and Engineering,University of Jinan,Jinan 250022,China)

作者机构：School of Materials Science and EngineeringUniversity of Jinan 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2009年第24卷第6期

页      面：982-985页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National Natural Science Foundation of China (No.50672033) the "973"National Key Fundamental Research Plan ofChina (No.2009CB623101-1) 

主　　题：durability cement alite calcium barium sulphoaluminate 

摘      要：The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.