Thermal Stability of Retained Austenite in TRIP Steel After Different Treatments
Thermal Stability of Retained Austenite in TRIP Steel After Different Treatments作者机构:Department of Material Science and Engineering Shanghai University Shanghai 200072 China Laboratory for Iron and Steel Making Department of Material Science and Engineering Technologiepark 903 BE-9052 Ghent Belgium Department MTM KU Leuven Heverlee B-3001 Belgium
出 版 物:《Journal of Iron and Steel Research(International)》 (钢铁研究学报(英文版))
年 卷 期:2008年第15卷第1期
页 面:61-64页
核心收录:
学科分类:0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0703[理学-化学] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
基 金:Item Sponsored by National Natural Science Foundation of China(50171038) Belgium-China Bilateral Project BIL04/13
主 题:TRIP steel retained austenite thermal stability differential scanning calorimetry
摘 要:Thermal decomposition of retained austenite in TRIP steel was investigated by means of differential scanning calorimetry(DSC).The decomposition curve was abnormal,and the decomposition temperature and the activation energy were measured by the Kissinger method,which were all higher than those in quenched *** thermal decomposition data of samples soaked in liquid nitrogen after TRIP treatment were all similar to those without additional low temperature *** indicated that there is a high thermal stability in retained austenite of the TRIP steel at low temperature,which was also proved by XRD analysis.