STUDY OF TCP PHASE PRECIPITATING IN GH4199 SUPERALLOY

作     者：T.Cui Y.S.Zhang S.W.Guo L.Wang H.C.Yang 

作者机构：SchoolofMaterialsandMetallurgyNortheasternUniversityShenyang110004ChinaManuscriptreceived15July2003 inrevisedform19January2004 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：2004年第17卷第5期

页      面：645-650页

核心收录：

学科分类：0817[工学-化学工程与技术] 0806[工学-冶金工程] 08[工学] 0807[工学-动力工程及工程热物理] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0802[工学-机械工程] 0703[理学-化学] 0811[工学-控制科学与工程] 

主　　题：superalloy TCP phase electron hole number 

摘      要：The precipitating regulation and mechanism of TCP phase (μ phase and σ phase) are studied, using electron hole number (EHN) theory, phase analysis technology and TEM observation. The results indicate that the EHN in studied alloy is 2.311-2.348 which is higher than that of critical EHN of μ phase precipitate (2.30), so μ phase could precipitate if there is enough thermo-exposition. In contrast, the calculated EHN is less than that of critical EHN of σ phase precipitate (2.52). However the σ phase is also observed by TEM. Enrich of Cr and Mo around γ phase after γ′phase precipitated leads to σ phase precipitated.