Comparative Studies on Synthesis and Characterization of Titania and Iron Oxide Doped Magnesia from Indian Salem Magnesite
Comparative Studies on Synthesis and Characterization of Titania and Iron Oxide Doped Magnesia from Indian Salem Magnesite作者机构：Department of Metallurgical and Material Engineering Jadavpur University Kolkata India Department of Mechanical Engineering Colorado School of Mines Golden CO USA Department of Materials Engineering Indian Institute of Science Bangalore India
出 版 物：《Journal of Materials Science and Chemical Engineering》 (材料科学与化学工程（英文）)
年 卷 期：2016年第4卷第7期
页 面：67-76页
学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）]
主 题：Sintering Additive Magnesite Densification
摘 要：Sintering, densification, and characterization of Salem Magnesite with Titania (TiO2) and Iron Oxide (Fe2O3) addition have been carried out in this work. Salem Magnesite samples with 2 wt.% TiO2 and Fe2O3 addition have been sintered in the temperature range of 1550?C - 1650?C. The sintered sample has been characterized in terms of physico-chemical properties like bulk density, apparent porosity, specific gravity and structural properties by X-ray diffraction and scanning electron microscope (SEM). Salem magnesite samples with 2 wt.% TiO2 and Fe2O3 addition have been densified to the specific gravity of 3.75 and 3.41 g/cc respectively after sintering at 1650?C and 2 h. The presence of Calcium Titanate (CaTiO3) phase at the grain boundary has been observed in the case of TiO2 addition. For Iron Oxide addition, precipitation of “Y shaped magnesium ferrite spinel has been observed inside the grains. Finally, TiO2 addition in Salem Magnesite shows better densification compared to both as received Salem Magnesite and Salem Magnesite with Fe2O3 addition.
维普期刊数据库