Effect of Silica Fume on Mechanical Properties of Concrete Incorporating Steel Slag Powder

作     者：LUO Xiaobao SI Yayu GU Wanqing 

作者机构：School of Civil Engineering and ArchitectureAnhui University of Science and Technology 

出 版 物：《Wuhan University Journal of Natural Sciences》 (武汉大学学报（自然科学英文版）)

年 卷 期：2019年第24卷第1期

页      面：86-92页

核心收录：

学科分类：08[工学] 081304[工学-建筑技术科学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0813[工学-建筑学] 

主　　题：silica fume steel slag powder concrete compressive strength brittleness discreteness surface fitting 

摘      要：This study investigated the effect of silica fume(SF) on mechanical properties of concrete incorporating steel slag powder(SSP). The compressive strength and splitting strength tests of concrete with different content of SF(0%, 4%, 8% and 12%) and of SSP(0%, 10%, 20%, 30% and 40%) were carried out, and the test results were analyzed and fitted. Obtained results showed that the brittleness, compressive strength and compressive strength discreteness of concrete increased due to the incorporation of SF. SSP weakened the compressive strength of concrete, which reduced within 10% when the content of SSP was less than 20%. SF and SSP showed synergistic hydration effect when they were mixed, and the optimal group was SF8 SSP30, whose compressive strength was close to that of plain concrete, and whose brittleness as well as discreteness of compressive strength were lower relatively. With the content of SSF and of SSP as variables, the tension-compression ratio and compressive strength of concrete can be well estimated by surface fitting.