Synthesis and Properties of Perfluorinated Alkyl Silicone Oil Modified Epoxy Resin

作     者：孙明慧 MA Ben 翁睿 

作者机构：School of Materials Science and Engineering Wuhan University of Technology 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2014年第29卷第2期

页      面：361-366页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the National High Technology Research and Development Program("863"Program)(No.2003AA305071) 

主　　题：perfluorinated alkyl silicone oil epoxy resin modification 

摘      要：Perfluorinated alkyl silicone oil （PFASO） was successfully synthesized from N-ethyl-N- hydroxylethyl perfluorinated octane sulfonamide, succinie anhydride and amino silicone oil by esterification and amide reaction at moderate temperature in the presence of different catalysts. The chemical structure of the synthesized samples was characterized by Fourier transform infrared spectroscopy （FT-IR）, the relative molecular mass（MM） and molecular mass distribution（MMD） of PFASO were tested by gel filtration chromatography（GFC）. A commercial epoxy resin （DGEBA） was modified with PFASO, with the content of PFASO 1-5 phr. Thermo-gravimetric analysis （TGA）, impact tests, scanning electron microscope （SEM） and water contact angle test were applied to provide accurate results on the thermal stability, toughness and hydrophobicity of PFASO/epoxy complex. The experimental results reveal that epoxy resins can be successfully modified by adding a small amount of as-synthesized modifiers via simple direct mixing, and verify that the as-synthesized modifier can improve the toughness and hydrophobicity of epoxy resin without sacrificing its thermal properties.