Compressive Strength, Pore Size Distribution and Chloride-ion Penetration of Recycled Aggregate Concrete Incorporating Class-F Fly Ash

作     者：寇世聪 C S Poon 

作者机构：Department of Civil and Structural EngineeringThe Hong Kong Polytechnic University Hung HomKowloon Hong Kong 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2006年第21卷第4期

页      面：130-136页

核心收录：

学科分类：08[工学] 081304[工学-建筑技术科学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 0813[工学-建筑学] 0702[理学-物理学] 

基　　金：Funded by the Environment and Conservation Fund  the WooWheelock Green Fund andthe Hong Kong Polytechnic University 

主　　题：durability properties recycled aggregate concrete fly ash 

摘      要：The effects of fly ash on the compressive strength, pore size distribution and chloride-ion penetration of recycled aggregate concrete were investigated. Two series of concrete mb：tures were prepared. The concrete mixtures in series I had a water-to-binder ratio and a cement content of 0.55 and 410 kg/ m^3 , respectively. The concrete rnixtures in series II had a water-to-binder ratio and a cement content of 0.45 and 400 kg/ ml respectively. Recycled aggregate was ased as 20% , 50% , and 100% replacements of natural coarse aggregate in the concrete mixtures in both series. In cutdition, fly ash was used as 0% , 25% and 35% by weight replacements of cement. The results show that the compressive strengths of the concrete decreased as the recycled aggregate and the fly ash contents increased. The total porosity and average porosity diameter of the concrete increased us the recycled aggregate content increased. Furtherrruore , an increase in the recycled aggregate content decreased the resistance to chloride ion penetration. Nevertheless, the replacement of cement by 25% fly ush improved the resistance to chloride ion penetration and pore diameters and reduced the total porosity of the recycled aggregate concrete.