Effect of processing routes on microstructure and mechanical properties of 2014 Al alloy processed by equal channel angular pressing

作     者：P.VENKATACHALAM S.RAMESH KUMAR B.RAVISANKAR V.THOMAS PAUL M.VIJAYALAKSHMI 

作者机构：Department of Metallurgical and Materials EngineeringNational Institute of Technology Physical Metallurgy DivisionIGCAR 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2010年第20卷第10期

页      面：1822-1828页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：ECAP processing route 2014 aluminium alloy 

摘      要：Al-Cu alloy was deformed through equal channel angular pressing(ECAP) by routes A,Ba,Bc and C up to 5 *** was done using a 90° die for three different conditions,namely 1) as received,2) solutionised at 768 K for 1 h and 3) solutionised at 768 K for 1 h + aged at 468 K for 5 *** microstructure,microhardness and tensile strength were studied for all the three conditions and four *** improvement in hardness(HV 184 after five passes) and strength(602 MPa after three passes) was observed in solutionised and aged 2014 Al alloy deformed through route *** evolution was reasonably equiaxed in route Bc with aspect ratio of *** and aged 2014 Al alloy deformed through route Bc was identified to have better microstructure and mechanical property than the other processing routes and conditions.