Hot deformation behavior and processing maps of Ti-15Al-12Nb alloy

作     者：Ravindranadh Bobbili Vemuri Madhu Ravindranadh Bobbili;Vemuri Madhu

作者机构：Defense Metallurgical Research LaboratoryHyderabad 500058India 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2022年第41卷第7期

页      面：2316-2323页

核心收录：

学科分类：08[工学] 080502[工学-材料学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：Hot deformation Processing map Ti–15Al–12Nb 

摘      要：The isothermal hot compression tests of Ti-15Al-12Nb alloy under wide range of strain rates(0.01-10.00 s^(-1)and deformation temperatures(950,1000,1050,and 1100℃)were carried out using Gleeble-3500 thermo-simulation machine.A constitutive equation represented as a function of temperature,strain rate and true strain was developed,and the hot deformation appar-ent activation energy is calculated to be about 453 kJ·mol^(-1).By employing dynamic material model(DMM),the processing maps of Ti-15Al-12Nb alloy at various strains were *** efficiency of about 57%for power dissipation is obtained at high temperature and low strain *** to the high power dissipation efficiency and excellent processing ability in dynamic recrystallization(DRX)zone for metal material,the optimum processing conditions are selected as the temperature range of 1050-1100℃and the strain rate range of 0.01-0.10 s^(-1).Using transmission electron microscopy(TEM)studies,it is found that the dislocation density is directly associated with the value of processing *** is observed that when the processing effi-ciency is about 22%,the dislocation density is reasonably *** flow instability region occurs at strain rate of 10.00 s^(-1)with cracks,which should be avoided during hot processing to obtain the required mechanical properties.