MICROSTRUCTURE OF DIFFERENTLY TREATED Al-Mg-Sc-Zr ALLOYS
MICROSTRUCTURE OF DIFFERENTLY TREATED Al-Mg-Sc-Zr ALLOYS作者机构:1. Department of Materials Science and Engineering Central South University of Technology 410083 Changsha China
出 版 物:《Journal of Central South University》 (中南大学学报(英文版))
年 卷 期:1997年第9卷第1期
页 面:24-27页
核心收录:
学科分类:08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 080502[工学-材料学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
主 题:Al-Mg-Sc-Zr alloy microstructure Al_3 (Sc,Zr) coherent and non-coherent
摘 要:The microstructures of different treated Al-5Mg-0.5Sc-0. 1Zr alloys have been studied with opticalmicroscopy and transmission electron microscope (TEM). Coherent particles with the matrix were found inas-cast sample. composite Al3Sc/Al3Zr particles were found after 13 h homogenized treatment under 470℃.Coherent precipitates pinned dislocations and low-angle grain boundaries. and then restrained recrystallization. All kinds of particles of different treatments were not larger than 40nm. After high-temperaturestabilization treatments, most particles remain coherent with the matrix. The reasons of microstructurechange at different treated conditions have been analyzed.